Polymer Property : Tensile Strength, Yield = 303 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	303 MPa @Diameter 12.7 mm	43900 psi @Diameter 0.500 in
Kaiser 6040 T8 Rod & Bar 6040 is a lead-free alternative to 6262. The alloy offers very good machinability along with good corrosion resistance. It also has excellent coating acceptance (anodize response). It can be used in..
Tensile Strength, Yield	303 MPa @Strain 0.200 %, Temperature 316 Â°C	43900 psi @Strain 0.200 %, Temperature 601 Â°F
Haynes UltimetÂ® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio..
Tensile Strength, Yield	303 MPa @Strain 0.200 %, Temperature 204 Â°C	43900 psi @Strain 0.200 %, Temperature 399 Â°F
Haynes HastelloyÂ® C-22Â® alloy, 0.71-3.2 mm thick sheet, solution heat treated HASTELLOYÂ® C-22Â® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an..
Tensile Strength, Yield	303 - 407 MPa	44000 - 59000 psi	0.2% offset
Eagle Brass 19210 XP-10 Copper Iron, 1/2 Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f..
Tensile Strength, Yield	303 - 572 MPa	44000 - 83000 psi	0.2% offset
Eagle Brass 770 Nickel Silver 18%, 1/4 Hard 770 has good cold forming properties, is tarnish resistant and has very good spring properties. 770 does not become subject to embrittlement at lower temperature and it has excellent corrosion resi..
Tensile Strength, Yield	303 MPa	43900 psi	.0275 - .035 inches sheet thickness; ASTM A 370
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Commercial Steel (FS Type B), Standard Grade May be moderately formed. A specimen cut in any direction can be bent flat on itself without cracking.Information provided by AK Steel
Tensile Strength, Yield	303 MPa	43900 psi	.0275 - .035 inches sheet thickness; ASTM A 370
AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, Commercial Steel (CS Type B), Standard Grade May be moderately formed. A specimen cut in any direction can be bent flat on itself without cracking.Information provided by AK Steel