Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 3.50 MPa | 508 psi | At 100% elongation, across flow; ASTM D412 |
Advanced Elastomer Systems VistaFlex® 714-B Thermoplastic Rubber
(discontinued **) Description: A black high-flow thermoplastic elastomer especially designed for injection molding applications. It replaces soft thermoplastics such as SBS, SEBS, and PVC blends. Supplied as free-f.. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | At 100% elongation, across flow; ASTM D412 |
Advanced Elastomer Systems VistaFlex® 714-N Thermoplastic Rubber
(discontinued **) Description: A black high-flow thermoplastic elastomer especially designed for injection molding applications. It replaces soft thermoplastics such as SBS, SEBS, and PVC blends. Supplied as free-f.. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ASTM D638 |
Micropol Microcoat DG/EVA/214A Microground modified EVA copolymer Specially developed for high specification coating where metal/coating adhesion is of primary importance. Typically used on large flat surfaces, and when toughness, elasticity and excellent barrier .. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
Lucobit Lucofin® 1400MN Ethylene Butyl Acrylate Lucofin 1400MN is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin 1400MN is softer and more flexible than ethylene homopoly.. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
Lucobit Lucofin® 1400MN Powder Ethylene Butyl Acrylate Lucofin 1400MN Powder is a polar copolymer consisting of ethylene and butyl acrylate with low crystallinity. Due to its chemical structure Lucofin 1400MN Powder is softer and more flexible ethane et.. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ASTM D638 |
Micropol E188 Rotational molding powder based on a random EVA copolymer Information provided by Micropol Limited |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | at 100% elongation, maximum |
Dow Corning SILASTIC® 25787 SILICONE RUBBER NATURAL Information provided by Dow Corning |
|||
Tensile Strength, Yield | 3.50 MPa @Temperature 23.0 °C |
508 psi @Temperature 73.4 °F |
ASTM D638 |
DuPont™ Surlyn® 9320 Zinc Ionomer Surlyn® 9320 is a zinc ionomer thermoplastic resin. It is available for use in conventional extrusion and injection equipment, to create various sheets or shapes. Surlyn® 9320 thermoplastic resin .. |
|||
Tensile Strength, Yield | 3.50 MPa @Strain 100 % |
508 psi @Strain 100 % |
|
Daikin DAI-EL LT-302 Fluoroelastomer, Low Temperature Grade, 64% Fluorine Content Features: Flexible up to -30°C, excellent low temperature sealing.Information provided by Daikin Industries. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | chs 20 in/min; 100% elongation; ASTM D412 |
Diamond Polymers Softflex® 1302 Thermoplastic Elastomer Alloy Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ASTM D638 |
Arkema Group OREVAC® 9318 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre.. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | 50 mm/min |
Arkema Group Evatane® 1020 VN 5 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for molding flexible articles. Examples: fittings, rail pads, medical.ISO data provided by the manufacturer, Arkema. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | 50 mm/min |
Arkema Group Evatane® 1020 VG 5 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for flexible films with high mechanical properties. Examples: films, chemical bags, gloves.ISO data provided by the manufactur.. |
|||
Tensile Strength, Yield | 3.50 MPa | 508 psi | ISO 527 |
A. Schulman SCHULAMID® 6 MV14 Unreinforced Nylon 6 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 3.50 - 38.0 MPa | 508 - 5510 psi | Average value: 22.1 MPa Grade Count:57 |
Overview of materials for Ethylene Butyl Acrylate This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Butyl Acrylate". Each property range of values reported is minimum and maximum values of approp.. |