Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 3.00 MPa | 435 psi | ASTM D412 |
Polymax® Maxelast® P2950 TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | ISO 527 |
Polimeri Europa Greenflex® ML 60 Ethylene Vinyl Acetate Copolymer - Injection Molding, Compounding & Extrusion Greenflex ML 60 is an ethylene vinyl acetate copolymer (EVA) for injection molding, compounding and extrusion. Items produced with Greenflex ML 60 show very high elasticity.Main Applications: Gree.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | chs 20 in/min; ASTM D412 |
Network Polymers Softflex® 0150 Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 3.00 - 6.00 MPa @Temperature 120 - 120 °C |
435 - 870 psi @Temperature 248 - 248 °F |
Average value: 4.50 MPa Grade Count:2 |
Overview of materials for Polychlorotrifluoroethylene; Molded This property data is a summary of similar materials in the MatWeb database for the category "Polychlorotrifluoroethylene; Molded". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | Silicone Rubber; JIS K6249(Die #3)/ASTM D412 |
Fujipoly Industries FG-S Connector Fujipoly FG-S connectors have anisotropic conduction properties. The fine metal wires are embedded in a vertical orientation within the silicone rubber width of 0.40mm. Low resistance and high curre.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | Silicone Rubber; JIS K6249(Die #3)/ASTM D412 |
Fujipoly Industries FG-S Fine Connector Fujipoly FG-S connectors have anisotropic conduction properties. The fine metal wires are embedded in a vertical orientation within the silicone rubber width of 0.40mm. Low resistance and high curre.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | |
Fujipoly Industries Sarcon® 30U Thin-Film UR Sarcon UR is Fujipolys originally developed High Heat Conductive/Low Hardness Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Information prov.. |
|||
Tensile Strength, Yield | 3.00 MPa @Strain 100 % |
435 psi @Strain 100 % |
ISO 527-1/-2 |
Covestro Desmopan® DP 1970AW Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | 508 mm/min; ASTM D638 |
Dow Engage® 8411 Polyolefin Elastomer Description: Engage® 8411 polyolefin elastomer is an ethyleneoctene copolymer that offers excellent performance in durable injection molded industrial and consumer goods and compression molded gask.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | |
ACC MM850 Low Tear Condensation Cure 2-Part Molding Rubber Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: low viscosity, good resistance to styrene attack, easy degassing, low shrinkage, range of catalysts. Applications: sh.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | |
ACC MM918 Condensation Cure 2-Part Molding Rubber Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: high tear strength, picks up extremely fine details, low viscosity, good resistance to styrene attack, easy degassing.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | |
ACC MM925 Condensation Cure 2-Part Molding Rubber Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: high tear strength, picks up extremely fine details, low viscosity, good resistance to styrene attack, easy degassing.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | |
ACC MM928 Condensation Cure 2-Part Molding Rubber Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: high tear strength, picks up extremely fine details, low viscosity, good resistance to styrene attack, easy degassing.. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | 50 mm/min |
Arkema Group Evatane® 1080 VN 5 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for molding very flexible articles. Examples: gaskets, medical.ISO data provided by the manufacturer, Arkema. |
|||
Tensile Strength, Yield | 3.00 - 6.00 MPa @Temperature 120 °C |
435 - 870 psi @Temperature 248 °F |
ASTM D638 |
Arkema Group VOLTALEF® 300 HD PCTFE VOLTALEF® 300 HD is a chlorotrifluoroethylene powder. Used for compression molding, very good flow, non-flammable. Information provided by Arkema Group |
|||
Tensile Strength, Yield | 3.00 - 6.00 MPa @Temperature 120 °C |
435 - 870 psi @Temperature 248 °F |
ASTM D638 |
Arkema Group VOLTALEF® 302 PCTFE VOLTALEF® 302 is a chlorotrifluoroethylene dense powder. Used in particular for compression molding, non-flammable. Information provided by Arkema Group |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | |
ACC QMSkin 30 Specialist Molding 2-Part Condensation Cure Part of the Amber Chemical Group. Data provided by manufacturer. |
|||
Tensile Strength, Yield | 3.00 MPa | 435 psi | M100 |
3M Dyneon™ Aflas® FA-150P PTFE Fluoroelastomer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Non-incorporated cure polymer, 57%F in polymer with 19% Medium Thermal Carbon Black (N990), 4% Triallyl Isocyanurate (TAIC), 1% Percadox™ 14, 1% Sodium.. |