Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 295 MPa @Strain 0.200 %, Temperature 540 °C |
42800 psi @Strain 0.200 %, Temperature 1000 °F |
|
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 295 MPa @Strain 0.200 %, Temperature 650 °C |
42800 psi @Strain 0.200 %, Temperature 1200 °F |
|
Haynes 25 alloy, hot rolled and 1230°C solution annealed sheet Excellent high-temperature strength with good resistance to oxidizing environments up to 980°C for prolonged exposures and excellent resistance to sulfidation and excellent resistance to metal ga.. |
|||
Tensile Strength, Yield | 295 MPa @Strain 0.200 % |
42800 psi @Strain 0.200 % |
|
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
Tensile Strength, Yield | 295 MPa @Strain 0.200 % |
42800 psi @Strain 0.200 % |
Typical; Annealed at 1800°F (982°C) |
ATI Allegheny Ludlum AL 800™ Nickel-Base Alloy, UNS N08800 AL 800 alloy is nickel-iron-chromium alloys designed to resist oxidation and carburization at elevated temperatures. The nickel content makes the alloy highly resistant both to chloride stress-corr.. |
|||
Tensile Strength, Yield | 295 MPa @Strain 0.200 %, Temperature 760 °C |
42800 psi @Strain 0.200 %, Temperature 1400 °F |
|
Haynes 230® alloy, hot rolled and 1232°C solution annealed plate Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
Tensile Strength, Yield | 295 MPa @Strain 0.200 % |
42800 psi @Strain 0.200 % |
|
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |