Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D638 |
S&E Specialty Polymers GPP1005HF Series PP Application: UL94 V-2, Flame-retardant polypropylene compounds for injection molding applications.Information provided by S&E Specialty Polymers |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2 in/min; ASTM D638 |
Phillips 66 COPYLENE® CM500LN Polypropylene, Impact Copolymer, High Flow, Medium Impact, Nucleated, Lube, Injection Molding COPYLENE™ CM500LN is a very high melt flow, medium impact polypropylene copolymer resin, designed for injection molding applications requiring a good balance of properties with faster cycling capab.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Ineos Nova Zyntar® F7080 Developmental Flame Retardant Polystyrene
(discontinued **) Features: General purpose non-Deca based resin (does not combine with Decabromodiphenyloxide)Good indoor UV light color stability(grey colors)UL94 V-0 @ 1.5 mm for all colors Good aesthetics for inj.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Suprex Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | Type I, 2 in/min; ASTM D638 |
M. Holland Company CP500 Polypropylene Copolymer Features: High Flow, High Impact Resistance, Good StiffnessUses: Automotive, Interior Parts Closures, Household Goods, ToysApprovals: FDA 21 CFR 177.1520Processing Method: Injection MoldingInformati.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2 in/min; ASTM D638 |
Ineos TUB 121NTW HDPE TUB121 NTW is a natural high density bimodal polyethylene copolymer designed for extrusion of large diameter, thick wall piping for potable water, industrial and mining applications. When blended wi.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | |
Kraton® G1650 + PP blend + Talc (12/21/67) Unmodified polypropylene has high rigidity and good heat resistance, but poor impact resistance, especially at low temperatures. Blending KRATON D and G polymers with PP significantly improves the .. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Techmer ES HiFill® HDPE TM5 5% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 5% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | |
Spartech 2969-92 General Purpose PVC First choice for compounds meeting the stringent requirements of Spiral Hose, Automotive, Housewares, Farm Equipment, Coated Fencing and numerous other applications including Lawn & Garden Wheels. B.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Spartech PP5240 Calcium Carbonate Filled Homopolymer Offers improved stiffness versus unfilled materials. They offer substantial improvements in drop weight (Gardner) impact over both unfilled polypropylene and other types of filled polypropylene. Cal.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Spartech SP-2010 HIPS Polystyrene Sheet Description: Polystyrene SheetInformation provided by Spartech. |
|||
Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D-882 |
Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.006" thick) T-100/T-200 Features/Benefits: Outstanding heat and chemical resistance; High dielectric strength; Anti-stick properties; Can be chemically etched for bondability; Applications include laminate rele.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2"/min; ASTM D638 |
A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene DescriptionLP 554-01 is a narrow molecular weight homopolymer high-density polyethylene exhibiting toughness, rigidity and warpage resistance. ApplicationApplications of LP 554-01 include crates, t.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2"/min; ASTM D638 |
A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene DescriptionLP 554-01 is a narrow molecular weight homopolymer high-density polyethylene exhibiting toughness, rigidity and warpage resistance. ApplicationApplications of LP 554-01 include crates, t.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Washington Penn Homopolymer Polypropylene 30% Calcium Carbonate Filled Calcium carbonate-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug pa.. |
|||
Tensile Strength, Yield | >= 24.1 MPa | >= 3500 psi | ASTM D638 |
Total HDPE XT25N High Density Polyethylene, Pipe Resin Polyethylene: High molecular weight, bimodal pipe resin. PPI TR4 designation PE4710 /PE100 for demanding installations. Every batch certified to meet 2500 hrs PENT according to ASTM F1473.Charact.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2" (50mm) per min.; ASTM D638 |
Formosa Plastics Formolene® 2510W Medium Impact Copolymer Polypropylene Impact CopolymerApplications: Trans-white battery casesFormolene 2510W is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property balance and excellent dime.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Lubrizol Hipscon™ M-520 Static Control High Impact Polystyrene Hipscon™ M-520 is a conductive, carbon black filled, High Impact Polystyrene available as extruded sheet. Thermoformed trays are easily formed into deep pockets that maintain uniform static protec.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
A. Schulman POLYFORT™ FPP 1200 Calcium Carbonate-Filled Homopolymer Polypropylene DescriptionPolyfort® FPP 1200 is a 40% calcium carbonate-filled homopolymer polypropylene. Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2" (50mm) per min.; ASTM D638 |
Formosa Plastics Formolene® 2510A Injection Applications Polypropylene Impact Copolymer with Nucleating, Antistat AdditivesApplications: Closures, housewares, small appliances, battery cases and lids.Formolene 2510A is a medium impact copolymer of polypropylene charact.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2" (50mm) per min.; ASTM D638 |
Formosa Plastics Formolene® 6520A Injection Molding Polypropylene Impact CopolymerApplications: Closures, Housewares, Small Appliance ApplicationsFormolene 6520A is a medium impact copolymer of polypropylene characterized by its easy mold flow, physical property b.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2"/min; ASTM D638 |
A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene DescriptionLP 554-01 is a narrow molecular weight homopolymer high-density polyethylene exhibiting toughness, rigidity and warpage resistance. ApplicationApplications of LP 554-01 include crates, t.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
ExxonMobil HDPE BU46-055 High Density Polyethylene Resin Product Description: BU46-055 is a high molecular weight, high density polyethylene copolymer which contains a UV inhibitor. It possesses a combination of excellent processability, outstanding melt .. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Dow 6D43 Polypropylene Random Copolymer Resin OverviewConsistent processabilityGood spinning characteristicsComplies with U.S. FDA 21 CFR 177.1520 (c)3.1aDOW 6D43 Polypropylene Resin is intended for use in fiber spinning processes.Dow Announced.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 |
Dow DGDA-2475 NT High Density Polyethylene Resin DOW DGDA-2475 NT is produced using UNIPOL™ process technology. It is intended for use in corrugated pipe applications. It has been specifically designed for extrusion of corrugated pipes with the.. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Dow UNIPOL™ DGDA-5110 Polyolefin DGDA-5110 UNIPOL™ is designed for the manufacture of thermoformed truck liners and other sheet extrusion applications requiring toughness and good process-ability. Information provided by Dow |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Asahi Kasei Thermofil P6-9900-0570 Unfilled, Flame Retardant, Heat Stabilized Information provided by Asahi Thermofil |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
Techmer ES Statiblend® PP CO 99074 Availability: North AmericaForms: PelletsFeature: Copolymer and Semi ConductiveUL File Number: E157318Information provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 24.1 MPa | 3500 psi | TM R050-36 |
Resinlab® EP11HT Gray Filled Epoxy Adhesive Resinlab™ EP11HT Gray is a two part filled epoxy adhesive designed for bonding metals and plastics. It cures at room temperature to a tough, semi-rigid material. It has good wetting to most surfa.. |
|||
Tensile Strength, Yield | 24.1 - 30.16 MPa | 3500 - 4375 psi | ASTM D-882 |
Saint-Gobain Norton® MFA Fluoropolymer Film Features/Benefits:Outstanding clarityPerformance from -254°C (-425°F) to 230°C (446°F)Outstanding flex life and stress-crack resistanceOutstanding anti-stick release propertiesExcellent electric.. |