Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 23.8 MPa | 3450 psi | 2 in per min; ASTM D638 |
Network Polymers NPP 25-0803 Description: Copolymer PolypropyleneInformation provided by Network Polymers Inc. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | 5.1 mm/min; ASTM D638 |
PolyOne Geon™ L4605 Red 7640 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid) Information provided by PolyOne |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | aged in air at 100ºC for 4 days |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CM015 Polypropylene Impact Copolymer COPYLENE™ CM015 is low melt flow impact copolymer with a barefoot additive package and is designed for excellent processing in injection molding and extrusion applications.Applications: Injection M.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CM200LN-02 Polypropylene Impact Copolymer COPYLENE™ CM200LN-02 is specially designed for injection molding applications where an excellent balance of stiffness/impact and good cycle times are required.Applications: Injection molding applic.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | |
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N330 (HAF) Filler MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | 2 in/min (50 mm/min); ASTM D638 |
Ineos K44-11-128 HDPE Ineos K44-11-128 is a high molecular weight, high density polyethylene copolymer intended for large part blow molding where the finished product demands good physical performance and low color. Thi.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | ASTM D 638 |
Styrolution PS 6220 HIPS Excellent toughnessHigh glossDesigned for deep draw thermoformingInformation provided by Styrolution |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | ASTM D638 |
Washington Penn Medium Impact Copolymer 40% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | ASTM D638 |
Washington Penn Medium Impact Copolymer 50% Talc Filled Talc-filled polypropylene compounds have been tailored specifically to meet the requirements of each of the major automobile producers. Grades are available to meet FDA food and drug packaging requi.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | aged in air at 100ºC for 4 days |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | (2 in/min); ASTM D638 |
Phillips 66 COPYLENE® CM015G Polypropylene Impact Copolymer COPYLENE® CM015G is low melt flow impact copolymer with a barefoot additive package and is designed for excellent processing in injection molding and extrusion applications.Applications:Injection M.. |
|||
Tensile Strength, Yield | 23.8 MPa | 3450 psi | |
TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N330 (HAF) Filler MILLATHANE HT is a polyester millable polyurethane which has the ability to withstand elevated temperatures. Polyurethanes have been known for their excellent resistance to abrasion, impact, tear st.. |