Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	19.3 MPa	2800 psi	Type IV, 510 mm/min; ASTM D638
PolyOne Syncure™ System S100BL Polyethylene, Crosslinked (XLPE) Syncure™ S100BL system is a three part moisture crosslinkable compound. S100BL is a UL bullentinized sunlight resistant, low density, black cable insulation compound. Available in a RoHS compliant ..
Tensile Strength, Yield	19.3 MPa	2800 psi
Resinlab® CYNERGY CA6104 Adhesive Description: The CYNERGY 6100 SERIES products are used to bond metal to itself or other substrates. It is available in five standard viscosities.Application: The CYNERGY SERIES of the cyanoacrylates..
Tensile Strength, Yield	19.3 MPa	2800 psi
Resinlab® CYNERGY CA6105 Adhesive Description: The CYNERGY 6100 SERIES products are used to bond metal to itself or other substrates. It is available in five standard viscosities.Application: The CYNERGY SERIES of the cyanoacrylates..
Tensile Strength, Yield	19.3 MPa	2800 psi
Resinlab® CYNERGY CA6201 Adhesive Description: The CYNERGY 6200 SERIES products are for use in demanding applications where very fast cure speeds are required. Also used when difficult to bond and acidic surfaces are used such as EP..
Tensile Strength, Yield	19.3 MPa	2800 psi
Resinlab® CYNERGY CA6210 Adhesive Description: The CYNERGY 6200 SERIES products are for use in demanding applications where very fast cure speeds are required. Also used when difficult to bond and acidic surfaces are used such as EP..
Tensile Strength, Yield	19.3 MPa	2800 psi
Resinlab® CYNERGY CA6211 Adhesive Description: The CYNERGY 6200 SERIES products are for use in demanding applications where very fast cure speeds are required. Also used when difficult to bond and acidic surfaces are used such as EP..
Tensile Strength, Yield	19.3 MPa	2800 psi
Resinlab® CYNERGY CA6208 Adhesive Description: The CYNERGY 6200 SERIES products are for use in demanding applications where very fast cure speeds are required. Also used when difficult to bond and acidic surfaces are used such as EP..
Tensile Strength, Yield	>= 19.3 MPa	>= 2800 psi	ASTM D1708
Technetics Group Texolon™ 7865 PTFE (Unverified Data**) Virgin PTFE for those applications not requiring the premium qualities of 8764 sheet.PTFE CharacteristicsChemical ResistanceThermal StabilityCryogenic PropertiesLow Coefficient of FrictionLow Surfac..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
FiberfilÂ® PP-61/VO/NH Polypropylene Copolymer, Flame Retardant, non-halogenated, UL94 V0 Information provided by FIBERFIL Engineered Plastics
Tensile Strength, Yield	19.3 MPa	2800 psi	2 in/min; ASTM D638
Ineos K38-20-160 Polyethylene Copolymer K38-20-160 is a medium density polyethylene copolymer containing an organic yellow pigment system, designed specifically for the extrusion of natural gas pipe. It exhibits excellent long term stres..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
Spartech PP7230 Calcium Carbonate Filled High Impact Copolymer Provides the highest level of impact of all copolymers and are useful in applications where improved processing and stiffness are required versus unfilled copolymer materials.Information provided by..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D412
Teknor Apex APEXÂ® 90-P513A-80-NT Polyvinyl Chloride+PUR Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Forms-PelletsInformation provided by Teknor Apex Company
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
Westlake Plastics HIPS High Impact Polystyrene, Compression Molded Compression molded HIPS is a low cost plastic material that is easily machined and fabricated. It is frequently used for preproduction prototyping. HIPS is a FDA compliant use in food processing a..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
Total PSI 935E Polystyrene Polystyrene 935E is a high impact polystyrene exhibiting exceptional toughness for sheet and thermoforming applications.This polymer is an excellent choice for cups, food packaging, custom sheet and..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
Total PSI 945 Polystyrene Polystyrene 945 is designed for injection molding applications requiring superior toughness. This polymer is a high impact polystyrene with excellent gloss and falling dart properties. The impact an..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene DescriptionSchuLink XL 350 is a cross-linkable, high density polyethylene used from rotational molding. This resin offers high impact strength, good abrasion resistance, good stiffness, and excelle..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
Westlake Plastics HIPS High Impact Polystyrene HIPS is a low cost plastic material that is easy to machine and fabricate. It is often specified for low strength structural applications when impact resistance, machinability, and low cost are req..
Tensile Strength, Yield	19.3 MPa	2800 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Atomite Whiting Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
ExxonMobil Paxon™ 7003 Crosslinkable Rotational Molding Resin Product Description: Paxon™ 7000 series of crosslinkable mHDPE resins are designed to offer outstanding ESCR, toughness, thermal, impact and notch failure resistance. These resins are ideally suite..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
ExxonMobil Paxon™ 7004 Crosslinkable Rotational Molding Resin Product Description: Paxon™ 7000 series of crosslinkable mHDPE resins are designed to offer outstanding ESCR, toughness, thermal, impact and notch failure resistance. These resins are ideally suite..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D638
ExxonMobil Paxon™ 7203 Crosslinkable Rotational Molding Resin Product Description: Paxon™ 7000 series of crosslinkable mHDPE resins are designed to offer outstanding ESCR, toughness, thermal, impact and notch failure resistance. These resins are ideally suite..
Tensile Strength, Yield	19.3 MPa	2800 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DMDA-8980 NT 7 High Density Polyethylene Resin DOW DMDA-8980 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow
Tensile Strength, Yield	19.3 MPa	2800 psi
Dow HDPE 04452N High Density Polyethylene DOW HDPE 04452N resin is a narrow molecular weight distribution copolymer designed to offer good stress crack resistance and stacking strength with excellent impact strength. This resin has moderate..
Tensile Strength, Yield	19.3 MPa	2800 psi	50 mm/min cross speed; ASTM D638
DuPont™ Surlyn® 7930 Ionomer Resin, Lithium Surlyn® 7930 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with lithium ions. The amount of MAA and ne..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D-638
Axiall 12881 Wire & Cable Flexible PVC Flame retardant, specialty grade, 75°C rated jacket compound. Designed to present a unique clear, sparkling appearance to the finished cable.Information provided by Georgia GulfGeorgia Gulf became..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D-638
Axiall 19482 Wire & Cable Flexible PVC 105°C, VW-1 rated non-lead stabilized insulation compound. Ideally suited for 18 AWG, 1/64 wall. UL approved for TW, THW, THHW applications.Information provided by Georgia GulfGeorgia Gulf became..
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D-638
Axiall 19880 Wire & Cable Flexible PVC 105°C rated, 30 mil and larger, clear compound recommended for VW-1 applications.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	19.3 MPa	2800 psi	ASTM D-638
Axiall 38511 Wire & Cable Flexible PVC Tray cable jacket with excellent low temperature properties.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
Tensile Strength, Yield	19.3 - 45.0 MPa	2800 - 6530 psi	Average value: 34.2 MPa Grade Count:35
Overview of materials for Polypropylene, Sheet/Thermoforming Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Sheet/Thermoforming Grade". Each property range of values reported is minimum and maximum..
Tensile Strength, Yield	19.3 MPa	2800 psi	2" (50mm) per min.; ASTM D638 Type IV
Formosa Plastics Formolene® HP3902 Pipe HDPE Natural Medium Density Hexene CopolymerApplications: Pipe for gas distribution, oilfield and other industrial pipe, telecommunications conduit.Formolene HP3902 is a high performance copolymer that i..