Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W1800L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable WELB406L Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 50 mm/min; ASTM D638 |
Polimeros Mexicanos Rotolene® 93050 Medium Density Polyethylene Hexene Copolymer Linear Medium Density Polyethylene for rotational molding. This resin is fully UV8 stabilized.Recommended for general purpose applications. Frequently used for water tanks (less tha.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 2 in/min; ASTM D638 |
Polimeros Mexicanos Rotolene® Industrial Black Linear Medium Density Polyethylene Hexene Copolymer Linear Medium Density Polyethylene grade which is fully UV8 stabilized. High quality Polyethylene compounded in black, formulated for rotational molding applications requiring excel.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6010 Adhesive Description: The CYNERGY 6000 SERIES are for use in demanding applications where very fast cure speeds are required. These are single component solvent free materials manufactured in a wide variety.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6011 Adhesive Description: The CYNERGY 6000 SERIES are for use in demanding applications where very fast cure speeds are required. These are single component solvent free materials manufactured in a wide variety.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6013 Adhesive Description: The CYNERGY 6000 SERIES are for use in demanding applications where very fast cure speeds are required. These are single component solvent free materials manufactured in a wide variety.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6813 Adhesive Description: The CYNERGY 6800 SERIES are clear, high strength products ideal for bonding dissimilar materials with excellent performance on a wide range of surfaces. This series of products has USP .. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 2" (50mm) per min.; ASTM D638 |
Formosa Plastics Formolene® L63565U Rotational Molding LLDPE
(discontinued **) Hexene CopolymerApplications: Toys, medium tanks, material handling equipment and flat surface rotational molding applications.Formolene L63565U is fully heat and UV stabilized.Meets all requirement.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Mistron Vapor Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6802 Adhesive Description: The CYNERGY 6800 SERIES are clear, high strength products ideal for bonding dissimilar materials with excellent performance on a wide range of surfaces. This series of products has USP .. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6810 Adhesive Description: The CYNERGY 6800 SERIES are clear, high strength products ideal for bonding dissimilar materials with excellent performance on a wide range of surfaces. This series of products has USP .. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 150x10x4 mm specimen, 50 mm/min; ISO 527-1/527-2 |
LyondellBasell SEQUEL® 1480 Engineered Polyolefin Description: SEQUEL® 1480 engineered polyolefin material is designed for large automotive exterior applications that require ductile impact properties at low temperatures, excellent paintability,.. |
|||
Tensile Strength, Yield | 18.6 MPa @Thickness 3.20 mm |
2700 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical LUPOL TE5208 PP+Rubber+MF, High Impact Description: Injection Molding, PP+Rubber+MF, High Impact, Good WeatherabilityApplication: Automotive Exterior (Bumper Fascia, Rear Bumper Step)Information provided by LG Chemical |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SGH 3500 Polyvinyl Chloride, Flexible Availability: Asia Pacific Uses: Garden Hose Forms: Pellets Processing Method: ExtrusionInformation Provided by Teknor Apex |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | Longitudinal |
Saint-Gobain Norton® Fluorglas® Chemfilm® R167 Extruded Expanded PTFE Film (0.006" thick) Description: Expanded Unsintered Films are used in microwave and coaxial cable applications in which low dielectric constant and high velocities are required. R167-nominal density of 0.7 g/cc. R165-.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SFE 3500 Polyvinyl Chloride, Flexible Availability: Asia Pacific Features: Food Contact Acceptable; Non-Toxic Uses: Hose; Tubing Forms: Pellets Processing Method: ExtrusionInformation Provided by Teknor Apex |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SPF 3520 Polyvinyl Chloride, Flexible Availability: Asia Pacific Features: High Stiffness Uses: Gaskets; Profiles; Seals Forms: Pellets Processing Method: ExtrusionInformation Provided by Teknor Apex |
|||
Tensile Strength, Yield | >= 18.6 MPa | >= 2700 psi | Heat Aging (7 Days at 121°C); ASTM D412 |
Borealis Visico™/Ambicat™ ME4425/LE4476 Ambient Curing, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation Visico LE4423 is a natural, ethylene vinyl silane copolymer that, when combined with the catalyst masterbatch Ambicat LE4476, will undergo an accelerated, moisture-induced crosslinking reaction. Th.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 2" (50mm) per min; ASTM D638 |
Formosa Plastics Formolene® 2706N Impact Copolymer Polypropylene Copolymer for Heavy Duty Injection Molded Applications Formolene® 2706N is a copolymer of polypropylene designed and formulated for injection molding applications. It contains a unique combination .. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Zylog Hipolyene® 5198 FLM Thermoplastic Polyolefin & PP Compound Information provided by Zylog Plastalloys Pvt. Ltd. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 9.8 in/min; ASTM D638 |
Teknor Apex Sinvicomp SIH 7005A Polyvinyl Chloride, Flexible Availability: Asia Pacific Features: Good Stiffness; High Heat Resistance Uses: Wire and Cable Applications Wire Types: V-90HT Agency Ratings: AS 3147-1992 Forms: Pellets Processing Method: Extrusio.. |
|||
Tensile Strength, Yield | >= 18.6 MPa | >= 2700 psi | Heat Aging (7 days at 121°C); ASTM D412 |
Borealis Visico™ ME4425/LE4437 Scorch Retardant, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation Visico ME4425/LE4437 is a natural, moisture-induced crosslinking polyethylene compound that is designed for use as low voltage wire insulation and jacketing. ME4425 is a medium-density ethylene vin.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | 50 mm/min cross speed; ASTM D638 |
DuPont™ Surlyn® 9120 Ionomer Resin, Zinc Surlyn® 9120 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D-638 |
Axiall EX1188A Wire & Cable Flexible PVC UL 360 jacket compound. 80°C air; 60°C oil.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D-638 |
Axiall 22950 Coax & Telecom Flexible PVC Riser jacket, 25 mil over HDPE primaries.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D-638 |
Axiall 16900 Wire & Cable Flexible PVC Tray cable jacket. 720 hour sunlight resistant in all colors.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D638 |
ExxonMobil Escorene® HD-8660 LHDPE Rotational Molding Grade
(discontinued **) Data provided by the manufacturer, Exxon Chemical.HD-8600 series are linear high density polyethylene resins that provide outstanding environmental stress crack resistance. HD-8660 is fully formula.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6904 Adhesive Description: The CYNERGY 6900 SERIES are for use in demanding applications where very fast cure speeds and high temperature resistance are required. These are single component solvent free materials.. |
|||
Tensile Strength, Yield | 18.6 MPa | 2700 psi | |
Resinlab® CYNERGY CA6908 Adhesive Description: The CYNERGY 6900 SERIES are for use in demanding applications where very fast cure speeds and high temperature resistance are required. These are single component solvent free materials.. |