Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 169 MPa | 24500 psi | ASTM D638 |
PolyOne LubriOne™ NL-30CF/15T Black Polyamide 612 (Nylon 612) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | Type I, 5.1 mm/min; ASTM D638 |
PolyOne Nymax™ GF 924 33 UV Black 108 Polyamide 66 (Nylon 66) Property data for molded test bars: Dry as MoldedInformation provided by PolyOne |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | 50 mm/min; ASTM D638 |
Ovation Polymers UTTAP SF 50030GF Polyethersulfone, 30% Glass Reinforced Glass reinforced (30 %) Polyether Sulfone, excellent chemical and electrical resistance, high stiffness, modulus and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50%.. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | 50 mm/min; ASTM D638 |
Ovation Polymers UTTAP™ SF 50030 GF Polyether Sulfone, 30% Glass Fiber Excellent chemical and electrical resistance, high stiffness, modulus and HDTAll properties after 48hrs conditioning at 23°C/50% RH |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | ASTM D638 |
GEHR Plastics Ultem 2300 PEI-30 GF 30% Glass Fiber Reinforced
(discontinued **) Polyetherimide has a high mechanical strength in connection with a good chemical and heat resistance, good dimensional stability and great resistance. It's unique torque strength permits the econom.. |
|||
Tensile Strength, Yield | 169 MPa @Strain 0.200 %, Temperature 982 °C |
24500 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RFG16S PA 66 LNP* LUBRICOMP* RFG16S is a compound based on Nylon 66 resin containing 5% Graphite, 30% Glass Fiber. Added features of this material include: Heat Stabilized, Wear Resistant. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | ASTM D638 |
Techmer ES HiFill® PA6 GF33 UG HS BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Lubricant and Heat Stabilizer Features: General Purpose, Lubricated and Heat S.. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON REL33 PA 66 LNP STAT-KON* REL33 is a compound based on Nylon 66 resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | ASTM D638 |
Techmer ES HiFill® PPS GF40 TL13 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: PTFE LubricantFeatures: LubricatedInformation provided by TP Composites, Inc. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI (Europe-Africa-Middle East) LNP* THERMOCOMP* EF006 is a compound based on Polyetherimide resin containing Glass Fiber. |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | ASTM D638 |
Ashley Polymers Ashlene® 990L-40G Nylon 610, 40% Glass Reinforced 40% glass reinforced, excellent dimensional stability and low water absorption. Also available as: 990LS-40G, same with heat stabilizer.Data provided by the manufacturer |
|||
Tensile Strength, Yield | 169 MPa | 24500 psi | .0275 - .035 inches sheet thickness; ASTM A 370 |
AK Steel ZINCGRIP® ELECTRASMOOTH® Electrogalvanized Carbon Steel, Extra Deep Drawing Steel Plus (EDDS+), Standard Grade Interstitial Free (I-F) steels are made by adding titanium to the molten steel after degassing and offer excellent drawability.Information provided by AK Steel |