Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 142 MPa | 20600 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® AR-6508 PBT/PET, Glass Filled Good WeatherabilityInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 142 MPa | 20600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10 (Europe-Africa-Middle East) LNP* THERMOCOMP* QF0069 is a compound based on PA610 resin contaning Glass Fiber, Flame Retardant. Added features include: Flame retardant. |
|||
Tensile Strength, Yield | 142 MPa | 20600 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP JCL36E PES LNP* LUBRICOMP* JCL36E is a compound based on Polyethersulfone (PES) resin containing 30% Carbon Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength, Yield | 142 MPa | 20600 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® AR-6508 PBT/PET, Glass Filled Good WeatherabilityInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 142 MPa | 20600 psi | SABIC - Japan Method |
SABIC Innovative Plastics Noryl GTX GTX6801 PPE+PS+PA66 (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength, Yield | 142 MPa | 20600 psi | ASTM D638 |
Cheng Yu Plastic N6GV20 Flame Retardant Nylon 6, 20% Glass Filled |
|||
Tensile Strength, Yield | 142 MPa @Temperature -40.0 °C |
20600 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8202C HS PA6 (Conditioned) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also.. |
|||
Tensile Strength, Yield | 142 MPa @Temperature -40.0 °C |
20600 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8202C HS PA6 (Conditioned) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also.. |
|||
Tensile Strength, Yield | 142 MPa @Temperature -40.0 °C |
20600 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength, Yield | 142 MPa @Temperature -40.0 °C |
20600 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8202C PA6 (Conditioned) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength, Yield | 142 MPa @Temperature -40.0 °C |
20600 psi @Temperature -40.0 °F |
ISO Data |
BASF Ultramid® 8202CQ PA6 (Conditioned) Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme.. |
|||
Tensile Strength, Yield | 142 MPa @Temperature -40.0 °C |
20600 psi @Temperature -40.0 °F |
ASTM Test |
BASF Ultramid® 8202CQ PA6 (Conditioned) Ultramid 8202CQ is a low viscosity, PA6 injection molding homopolymer, possessing a modified crystalline structure or increased property performance and faster cycles. It is also available in pigme.. |