Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 118 MPa | 17100 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36 PC LNP* LUBRICOMP* DFL36 is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36XXP PC LNP* Lubricomp* DFL36XXP is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 118 - 179 MPa | 17100 - 26000 psi | Average value: 153 MPa Grade Count:4 |
Overview of materials for Nylon 66, Glass Fiber/PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber/PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Yield | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUCON SP9306FL sPS+MF Description Injection Molding Grade, sPS+MF, Low Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts CAS No. 9003-53-6, 65997-17-3, 68928-70-1 .. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM D638 |
LG Chemical LUPOS HR-2207 Heat Resistant SAN, 20% Glass Fiber Reinforced LUPOS resins are glass fiber reinforced styrene copolymers. LUPOS have improved strength, rigidity and dimensional stability. They offer excellent heat resistance, minimal mold shrinkage and have .. |
|||
Tensile Strength, Yield | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUPOY GP2300 PC+GF30%, Heat Resistance Description: Injection Molding, PC+GF30%, General Purpose, Heat ResistanceApplication: IT/OA, E&E Housing and Components, Automotive (Interior)CAS: 103598-77-2 and 65997-17-3Information provided by .. |
|||
Tensile Strength, Yield | 118 MPa @Thickness 3.20 mm |
17100 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
LG Chemical LUPOY GN2301F PC+GF30%, Halogen Free, Flame Retardant, Heat Resistance Description: Injection Molding, PC+GF30%, Halogen Free Flame Retardant, Heat ResistanceApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2 and 65997-17-3Information prov.. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA6.10 (Europe-Africa-Middle East) LNP* LUBRICOMP* QFP36 is a compound based on PA6.10 resin containg Glass Fiber, PTFE, Silicone. Added features include: Internally Lubricated. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 LNP* LUBRICOMP* RFL33 is a compound based on Nylon 66 resin containing 15% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RFL33 PA 66 (Asia Pacific) LNP* Lubricomp* RFL33 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP WFL34 PBT LNP LUBRICOMP* WFL34 is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP GF006 PSU (Europe-Africa-Middle East) LNP* THERMOCOMP* GF006 is a compound based on Polysulfone resin containing Glass Fiber. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® GP-8300G MPPE, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2165M PPS Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® GP-5300G PBT, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® GP-8300G MPPE, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HM-3301GL PC, Glass Filled High Impact PC/GF material that is used for electric and electronic partsInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HT-8200G MPPE/PA, Glass Filled Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 5 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® XP-2165M PPS Information provided by Samsung Cheil Industries. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DE0039 PC (Asia Pacific) LNP* Stat-kon* DE0039 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM 638 |
PlastxWorld CEVIAN® B5526 30% GF PBT/ABS Alloy Glass fiber reinforced and flame retarded PBT/ABS alloy.Information provided by PlastxWorld Inc. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM D638 |
Cheng Yu Plastic ML3430 PC, 30% Glass Fiber |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM D638 |
Cheng Yu Plastic N6GV10 Flame Retardant Nylon 6, 10% Glass Filled |
|||
Tensile Strength, Yield | 118 MPa @Temperature 23.0 °C |
17100 psi @Temperature 73.4 °F |
EN ISO 527 |
Ensinger TECASINT™ 2011 Polyimide (PI) TECASINT™ 2000 series of polyimide stock shapes provide a superior combination of high temperature and bearing and wear, properties that make it an ideal choice for the most demanding applications... |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM D638, ISO R527 |
EPICHEM Epiter PBT GF 20 Polybutylene Terephthalate, 20% Glass Characteristics: 20% glass fibre filled |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | 50mm/min; ISO 527-2 |
BASF Ultradur B 4300 G4 High Speed Unc. 20% Glass Filled PBT Ultradur B 4300 G4 High Speed Unc. is a high flow, fast cycling with low warpage, 20% glass filled, pigmented black, injection molding PBT for industrial parts, rigid tough and dimensional stable ap.. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66 Preliminary data for 20% long glass fiber filled, single pellet color gray, PA66This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 118 MPa | 17100 psi | ASTM 638 |
PlastxWorld CEVIAN® B2706 30% GF PBT/ABS Alloy Glass fiber reinforced PBT/ABS alloy.Information provided by PlastxWorld Inc. |