Polymer Property : Tensile Strength, Yield = 11.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D412
Polymax® Maxelast® P3885M TPE, PP Overmold or Standalone use Polymax's TPE material complies with UL, VDE, FDA, RoHS and PAH's standards.Uses:Consumer ProductsToys & NoveltiesAuto PartsTool Hand GripsSporting GoodsWire & Cable ElectronicsMedical DevicesPlasti..
Tensile Strength, Yield	11.7 MPa	1700 psi	-10% change after 70 hours @ 100°C; ASTM D412
Precision Polymer Engineering N60W Nitrile Rubber White Nitrile Butadiene Rubber (NBR), 55-65 °IRHD. Copolymer of acrylonitrile and butadiene. Formulated using only those ingredients determined by the United States Food and Drug Administration (F..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
M. Holland Company LD800 LDPE (discontinued **) Features: High Clarity, High Flow, Narrow Molecular Wt. Dist., Good Processability, Warp ResistantUses: Closure Caps, Drink LidsApprovals: FDA 21 CFR 177.1520(c) 2.2 and ASTM D 1248, I, Class A, Cat..
Tensile Strength, Yield	11.7 MPa	1700 psi
TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 10 PHR Iceberg Clay Filler MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subje..
Tensile Strength, Yield	11.7 MPa	1700 psi	ISO 1184-1983E
LyondellBasell Montell 8640 Polybutene-1 Key Features: semi-crystalline low ethylene content random copolymer, miscible with polypropylenes, FDA acceptableApplications: minor additive in a polyethylene peel seal layerMeets FDA requirements..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
LyondellBasell PetrotheneÂ® GA808091 Linear Low Density Polyethylene ApplicationsPETROTHENE GA 808-091 is a broad molecular weight, linear low density polyethylene resin designed for use as a base resin in wire and cable jacketing. An antioxidant package is added to..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
Micropol E332 Rotational molding powder based on a random EVA copolymer Information provided by Micropol Limited
Tensile Strength, Yield	11.7 MPa	1700 psi	at 100%; ASTM D412
Multibase Multi-FlexÂ® D 4701 TPE Thermoplastic Elastomer Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good I..
Tensile Strength, Yield	11.7 MPa	1700 psi	Elastic; ASTM D412
Multibase Multi-FlexÂ® G 7715 TPE Styrene Ethylene Butylene Styrene Block Copolymer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
Tensile Strength, Yield	11.7 MPa	1700 psi	Elastic; ASTM D412
Multibase Multi-FlexÂ® A 9002 Black TPE Thermoplastic Elastomer Forms: PelletsProcessing Methods:Injection Molding Information provided by Multibase
Tensile Strength, Yield	11.7 MPa	1690 psi
Spartech 2850-50 PVC for Regulated Applications Information provided by Spartech
Tensile Strength, Yield	11.7 MPa	1700 psi
Spartech 2850-60 PVC for Regulated Applications Information provided by Spartech
Tensile Strength, Yield	11.7 MPa	1700 psi	Longitudinal
Saint-Gobain NortonÂ® FluorglasÂ® ChemfilmÂ® R167 Extruded Expanded PTFE Film (0.010" thick) Description: Expanded Unsintered Films are used in microwave and coaxial cable applications in which low dielectric constant and high velocities are required. R167-nominal density of 0.7 g/cc. R165-..
Tensile Strength, Yield	11.7 MPa	1700 psi	after aging 1 week @ 135°C; ASTM D638
Trelleborg Horda Cable E8561 Strippable Semiconductive Shielding E8561 is a vulcanizing, strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes.E8561 meets the requirements as bel..
Tensile Strength, Yield	11.7 MPa	1700 psi	50 mm/min cross speed; ASTM D638
DuPont™ Surlyn® 9720 Ionomer Resin, Zinc Surlyn® 9720 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Tensile Strength, Yield	11.7 MPa	1700 psi	50 mm/min cross speed, ASTM D638
DuPont™ Surlyn® 9721 Ionomer Resin, Zinc Surlyn® 9721 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LDPE LD 101BA Wire & Cable Low Density Polyethylene Resin Product Description: LD 101BA Wire & Cable is anon-stabilized LDPE, designed for the production of Medium/High Voltage insulation using the direct peroxide addition. For cleanliness reasons, the mat..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LDPE LD 419.MV Low Density Polyethylene Resin Product Description: LD 419.MV is a LDPE designed for wire and cable applications and is suitable for making crosslinkable compounds for medium voltage insulation.Availability: Latin America, North ..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LL 6201.19 Injection Molding Resin Product Description: LL 6201 is a narrow molecular weight butane copolymer designed for applications that require excellent toughness. This resin offers easy processability for applications that req..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LLDPE LL 1004YB Wire & Cable Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 1004YB is a C4 Ziegler Natta LLDPE, especially designed for Low Voltage power cable insulation, using the two-step silane cross-linking process. The grade contains a higher l..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LLDPE LL 5002.09 Linear Low Density Polyethylene Resin Product Description: LL 5002.09 is a linear low density polyethylene resin designed to provide good processability and ease of blending. LL 5002.09 also exhibits good toughness and environmental str..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D638
ExxonMobil LLDPE LL 6100.17 Linear Low Density Polyethylene Resin Product Description: LL 6100 is a narrow molecular weight butane copolymer designed for applications that require easy processability. This resin offers outstanding toughness and tear resistance in ..
Tensile Strength, Yield	11.7 MPa	1700 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow DNDA-8320 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-8320 NT 7 is produced using UNIPOL™ PE process technology. It is intended for use in general purpose injection molding applications. Information provided by Dow
Tensile Strength, Yield	11.7 MPa	1700 psi	Molded and tested in accordance with ASTM D4976; ASTM D638
Dow GRSN-9820 NT 7 Linear Low Density Polyethylene Granular Solid DOW GRSN-9820 NT 7 is produced using UNIPOL™ PE process technology and is supplied in granular form. This resin is specifically designed as a carrier resin for color concentrates and other master ..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 2134N Moldings & Extrusions Flexible PVC 105C plug molding compound. UL recognized component for 94 V-2 in all colors (0.75 mm min. thickness) and 94 V-0 in black and white (1.5 mm min. thickness). UL QMFZ2 recognized component.Informati..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 7810 Moldings & Extrusions Flexible PVC 105°C rated injection molding compound approved for 94 V-0 in black and white at 0.75 mm and also approved for 94 V-0 in all colors at 1.5 mm.Information provided by Georgia GulfGeorgia Gulf became..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D412
Teknor Apex APEX® 3202-60 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Caps, Closure, Connectors, Food Service Applications, Safety Equipment, Valves/Valve Parts Appearance-Cl..
Tensile Strength, Yield	11.7 MPa	1700 psi	100%; ASTM D412
Teknor Apex APEX® 3311-85 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTM Uses-Automotive Applications, Food Service Applications, General Purpose, Medical Applications, Profiles, To..
Tensile Strength, Yield	>= 11.7 MPa	>= 1700 psi
Trelleborg Offshore Vikotherm™ 73165 Insulative Elastomer Vikotherm™ is a rubber elastomer chemically modified to provide very high insulating characteristics while maintaining its inherent rubber properties in respect of seawater resistance, pressure res..
Tensile Strength, Yield	11.7 MPa	1700 psi	ASTM D-638
Axiall 46234A Moldings & Extrusions Flexible PVC Automotive window encapsulation compound.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.