Polymer Property : Tensile Strength, Yield = 100 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ASTM D638
Ovation Polymers Opnyl OP66GF13 Nylon 66, 13% Glass Reinforced Nylon 66 - Glass reinforced (13 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Oxford Polymers PBT 15GF-V0 UL Listed Polybutylene Terephthalate (PBT) UL Listed Polybutylene Terephthalate (PBT)Information provided by Oxford Polymers.
Tensile Strength, Yield	100 MPa	14500 psi	Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638
PolyOne Edgetek® PK-1000 Polyetheretherketone (PEEK) (discontinued **) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Tensile Strength, Yield	100 MPa @Temperature 23.0 °C	14500 psi @Temperature 73.4 °F	ISO 527
Victrex® PEEK 90P Polyetheretherketone, Unreinforced Product Description:High performance thermoplastic material, unreinforced Polyetheretherketone (PEEK), semi crystalline, coarse powder for extrusion compounding, easy flow, FDA food contact complian..
Tensile Strength, Yield	100 - 175 MPa	14500 - 25400 psi	Average value: 144 MPa Grade Count:4
Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled". Specific grades with glass content between 25% an..
Tensile Strength, Yield	100 MPa @Strain 0.200 %, Temperature 980 Â°C	14500 psi @Strain 0.200 %, Temperature 1800 Â°F
Haynes 242Â® alloy, cold rolled sheet, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815Â°C, excellent low cycle fatigue properties, very good therm..
Tensile Strength, Yield	100 MPa	14500 psi	ISO-DIS 527
Schwartz Technical Plastics MITELAÂ® HD8B Cotton Fabric, Special Quality Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH
Tensile Strength, Yield	100 MPa	14500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM CRS5011R PEI (Asia Pacific) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Tensile Strength, Yield	100 MPa	14500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM CRS5011R PEI (Europe-Africa-Middle East) Enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics and ketones. Resin is RoHS compliant.
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Techmer ES HiFillÂ® ABS GF30 BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAppearance: BlackTPCI# 1018121Information provided by TP Composites, Inc.
Tensile Strength, Yield	100 MPa	14500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® 830F PBT+PET PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Tensile Strength, Yield	100 MPa	14500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump..
Tensile Strength, Yield	100 MPa	14500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics NORYL PX138H PPE+HIPS (Asia Pacific) Modified PPO Resin with 20% Glass Fibre Reinforced
Tensile Strength, Yield	100 MPa	14500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ULTEM UF5011S PEI (Europe-Africa-Middle East) Enhanced flow, Specialty filtered Polyetherimide (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics and ketones. ECO Conforming.
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527-2
Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced GB364WG is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. The product is available in natural but other colors can be provided on request. Th..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
PlastxWorld Veroplas PB3150 Nylon 66 15% glass filled injection molding gradeInformation provided by PlastxWorld Inc.
Tensile Strength, Yield	>= 100 MPa	>= 14500 psi	ISO 527
Polyram PlusTek RA303G3 Nylon 66 for Injection Molding, 15% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant 15% Glass fiber reinforced, heat stabilized and hydrolysis resistant Nylon 66 for injection molding applications.Information provided by Polyram.
Tensile Strength, Yield	100 MPa	14500 psi	D638
Zhejiang Juner 301-G25 25% Glass Fibre Reinforced and Flammable Resistant Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, ..
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527
Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized 15% Glass fiber reinforced, impact modified and UV stabilized Nylon 6 for injection molding applications.Information provided by Polyram.
Tensile Strength, Yield	100 MPa	14500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® GTR 45 PA6I/6T Product description: Grivory GTR 45 is a transparent engineering thermoplastic based on amorphous, partially aromatic copolyamide for injection molding. Compared to other semi crystalline polyamides..
Tensile Strength, Yield	100 MPa	14500 psi	dry; ISO 527-1/-2
DSM Stanyl® TW341-B PA46 Heat Stabilized, Lubricated
Tensile Strength, Yield	100 MPa	14500 psi	dry; ISO 527-1/-2
DSM Stanyl® TW341-J PA46 Heat Stabilized, Lubricated
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527-1/-2
DSM Stanyl® TW441 (DAM) Nylon 46 High Viscosity, Heat Stabilized, Lubricated (North America) Information provided by DSM Engineering Plastics.
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
E-Polymers TEKAMID® TB120GM20 , 20% GF/MF Reinforced PA6, DAM 20% GF/MF reinforced, Good surface, Low warpageInformation provided by E-Polymers Co. Ltd.
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
Aclo Accutech Polycarbonate POL050G20L Glass Reinforced
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ISO 527-1/-2
BASF Ultramid® KR 4350 PA6/6T (Dry) Description: For injection-molding and extrusion, exhibiting high toughness, strength and stiffness, low water absorption, high melting point (295 °C [563°F]). The mechanical properties remain con..
Tensile Strength, Yield	100 MPa	14500 psi	50 mm/min; ISO 527-2
BASF Ultradur® S 4090 G4X 20% Glass Filled PBT Description: Is a PBT + ASA, low-warpage, free-flowing injection-molding grades with very good processing capabilities, containing 20% of glass fibers for industrial parts with high dimensional stab..
Tensile Strength, Yield	100 MPa	14500 psi	ASTM D638
PlastxWorld Veroplas PA3150 Nylon 6 general purpose, 15% glass filled injection molding gradeInformation provided by PlastxWorld Inc.
Tensile Strength, Yield	100 MPa	14500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Valox® V9230CS PET (Europe-Africa-Middle East) 15% GF PET Injection Moulding grade, Heat and Color Stabilised, for light colorsThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Tensile Strength, Yield	100 MPa	14500 psi	ISO 527
Victrex® HT™ P45PF Polyetherketone Product Description: High performance thermoplastic material, unreinforced PolyEtherKetone (PEK), semi crystalline, fine powder for compression compounding, low flow, FDA food contact compliantInfor..