Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 10.3 MPa | 1490 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W7400 Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength, Yield | 10.3 MPa | 1490 psi | ASTM D412 |
Precision Polymer Engineering H70B Epichlorohydrin Peroxide Cured, Epichlorohydrin Rubber, 65-75 °IRHD. Terpolymer of epichlorohydrin, ethylene oxide and an unsaturated monomer. ASTM and ISO designation = GECO.Applications: Excellent resistance t.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
Quadrant EPP Proteus® LDPE - Low Density Polyethylene (ASTM Product Data Sheet) |
|||
Tensile Strength, Yield | 10.3 - 31.0 MPa | 1500 - 4500 psi | ASTM D638 |
Alcoa KAMA 3000 High Impact Polystyrene (HIPS)
(discontinued **) CapabilitiesGauge: .007” to .060” (178 to 1524µm)Width: 12” to 62” (304 to 1575mm)Core Size: 6” standard cores, 3” and 8” availableRoll O.D.: 29” standard, up to 40” availableMono-layer an.. |
|||
Tensile Strength, Yield | >= 10.3 MPa | >= 1500 psi | ASTM D638 |
Alcoa KAMA AgriHIPS 3500 AgriHIPS
(discontinued **) CapabilitiesGauge: .007” to .060” (178 to 1524µm)Width: 12” to 62” (304 to 1575mm)Core Size: 6” standard cores, 3” and 8” availableRoll O.D.: 29” standard, up to 40” availableSilicone coat.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1490 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1870A Polyethylene
(discontinued **) Polyethylene 1870A is a low density formulation with excellent flow characteristics for injection molding. It is used for such applications as container closures that require stress-crack resistanc.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | at 2% Offset; ASTM D638 |
ExxonMobil LD 503.LN Foams and Compounding Resin
(discontinued **) LD 503.LN is a low density homopolymer specially designed for maximum performance in foam applications.Information provided by ExxonMobil Chemical |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | at 2% Offset; ASTM D638 |
ExxonMobil LD 641.LN Molding, Extrusion and Compounding Resin
(discontinued **) LD 641.LN is a low density homopolymer specifically designed for high performance blow molding applications. This resin is suitable for applications requiring high melt strength, flexibility, good .. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
M. Holland Company LD500 LDPE
(discontinued **) Features: High Clarity, High Flow, Narrow Molecular Wt. Dist., Good Processability, Warp ResistantUses: Drink LidsApprovals: FDA 21 CFR 177.1520(c) 2.2 and ASTM D 1248, I, Class A, Cat. 1Processing .. |
|||
Tensile Strength, Yield | 10.3 - 252 MPa | 1500 - 36500 psi | Average value: 104 MPa Grade Count:75 |
Overview of materials for Nylon 66, 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 10% Glass Fiber Filled". Specific grades with glass content between 5% and 14% are included. .. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
LyondellBasell Petrothene® NA217080 Low Density Polyethylene ApplicationsPETROTHENE NA 217-080 is a natural low density polyethylene resin formulated for use as primary insulation for coaxial and control cable applications. NA 217-080 has also been designed .. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
LyondellBasell Petrothene® NA951080 Low Density Polyethylene ApplicationsPETROTHENE NA 951-080 is designed for use as a base resin for compounding material including gas-injected or chemically expanded insulation. NA 951-080 is a natural, low density, medium.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | |
Saint-Gobain Rulon® DC7035 Bearing/Seal PTFE Offers electrical conductivity in a low wear, self lubricating bearing material. This material is ideal in applications where static dissipation is needed. DC7035 is often used as a static bleed mec.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex APEX® 3201-60 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMUses-Automotive Applications, Non-specific Food Applications, General Purpose, Medical Applications, Modeling.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D412 |
Teknor Apex APEX® 3310-65 Polyvinyl Chloride, Flexible Material Status-Commercial: ActiveAvailability-North AmericaTest Standards Available-ASTMFeatures-Sterilizable, RadiationUses-Automotive Applications, Food Service Applications, General Purpose, Med.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D412-92 |
Saint-Gobain Versilicâ„¢ SPX-50 High Strength Silicone Tubing Formulation Description: Versilicâ„¢ SPX-50: Peroxide-cured Versilicâ„¢ High-Strength Silicone Tubing is designed for use in applications where flexibility, resiliency and durability are required. Its s.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1490 psi | ASTM D412 |
Teknor Apex TELCAR® 1000-92 Thermoplastic Elastomer Information provided by Teknor Apex Company |
|||
Tensile Strength, Yield | 10.3 MPa | 1490 psi | 2.0 in/min; ASTM D638 |
Teknor Apex Telcar® TL-1000-92-UV Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Automotive Spec.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
A. Schulman CP851 High Flow, Injection Molding Grade DescriptionCP 851 is a high flow injection molding grade of conventional (high pressure) low density polyethylene. ApplicationCP 851 meets the specifications in FDA Regulation 21 CFR177.1520 (c)3.1.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1490 psi | |
Zylog Hipolyene® 2703 MS Thermoplastic Polyolefin & PP Compound Information provided by Zylog Plastalloys Pvt. Ltd. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
ExxonMobil LLDPE L L6101RQ Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 6101 series are medium flow LLDPE grades, which offer excellent stiffness, heat distortion resistance and good environmental stress crack resistance. The excellent toughness .. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
ExxonMobil LLDPE LL 6101XR Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 6101 series are medium flow LLDPE grades, which offer excellent stiffness, heat distortion resistance and good environmental stress crack resistance. The excellent toughness .. |
|||
Tensile Strength, Yield | 10.3 MPa | 1490 psi | Molded property |
Dow DOWLEX™ 2047A Linear Low Density Polyethylene, Cast Film Grade DOWLEX® 2047A Polyethylene resin is a cast film polymer for high performance stretch cling applications. It provides outstanding tear strength, impact strength and toughness. It complies with U.S. .. |
|||
Tensile Strength, Yield | 10.3 MPa | 1490 psi | Molded property |
Dow DOWLEX™ 2247A Linear Low Density Polyethylene, Cast Film Grade DOWLEX® 2247A Polyethylene resin is a cast film polymer for applications requiring outstanding tear strength, impact strength and toughness. This material complies with U.S. FDA Regulation 21 CFR 1.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
Clariant Renol PA2SP0011HW Nylon 6, Heavyweight Compound Data provided by Clariant Masterbatches |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D-638 |
Axiall 8690 Moldings & Extrusions Flexible PVC General purpose extrusion compound designed for use in weatherstrips, screen spline and flexible gaskets.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D-638 |
Axiall 8770 Moldings & Extrusions Flexible PVC General purpose extrusion compound for weatherstrips, tubings and gaskets.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | 1:1; ASTM D412 |
ACC EP JS EPI Engineered Polymers Joint Sealant EP JS Joint Sealant JS, “Powered by Reactamine® Technology” is a two component 100% solid (silicone optional) polyurea based joint sealant. EP JS is a self-leveling joint sealant designed to prot.. |
|||
Tensile Strength, Yield | 10.3 - 27.6 MPa | 1500 - 4000 psi | ASTM D638 |
Alcoa KAMA 3202 Freezer Modified High Impact Polystyrene
(discontinued **) CapabilitiesGauge: .007” to .060” (178 to 1524µm)Width: 12” to 62” (304 to 1575mm)Core Size: 6” standard cores, 3” and 8” availableRoll O.D.: 29” standard, up to 40” availableColors availa.. |
|||
Tensile Strength, Yield | 10.3 MPa | 1500 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
PolyOne Synprene® RT-4080 Thermoplastic Elastomer - SBC, Mineral Filled
(discontinued **) Description/Features:Multi-Purpose Thermoplastic ElastomerMineral FilledApplications:Multi-PurposeMarket:AutomotiveBuilding and ConstructionIndustrialConsumer GoodsProcessing Method:ExtrusionInforma.. |