Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ASTM D882 |
SABIC F01552 High Density Polyethylene for Blown Film Product Description: F01552 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weigh.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | |
Premix Thermoplastics PREFLEX E12.5 Polyphenylene Ether (PPO/PPE) PREFLEX films combine outstanding dielectric properties, good heat stability, low water absorption and chemical resistance in a way not available before. Also rigid boards made of the same material .. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ASTM D882 |
Chevron Phillips HiD® 9632 HDPE Blown Film Resin
(discontinued **) Characteristics: Copolymerization Enhances Film Toughness, Excellent Film Drawdown Ideally Suited for Thin Films Production, Lower Melt Index (Higher Molecular Weight) Results in Increased Film Stre.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ASTM D882 |
Reliance Industries Relene F46003 Polyethylene Relene F46003 is a High Density Polyethylene grade suitable for producing blown parts with superior stiffness and barrier properties. It is recommended for making liners and coextruded film structu.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ASTM D882 |
Reliance Industries Relene F56003 Polyethylene Relene F56003 is a High Density Polyethylene grade suitable for producing blown parts with excellent drawdown and paper like feel. It is recommended for making carrier bags and coextruded film stru.. |
|||
Film Tensile Strength at Break, MD | <= 55.0 MPa | <= 7980 psi | ISO 527-1.3 |
Iran Petrochemical (PCC) MF3313 High Density Polyethylene MF3313 is a high molecular weight high density polyethylene . Applications: extrusion, film, blown, bags, and density modifies.Information provided by Iran Petrochemical Commercial Co. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
Borealis Borstar® FB2230 LLDPE for Film Borstar BF2230 is a high molecular weight low density polyethylene film grade combining good and flexible extrusion behavior, excellent draw down and superior mechanical properties. Film made from .. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
Topas Advanced Polymers TOPAS® 6013F-04 Cyclic Olefin Copolymer (COC) TOPAS® 6013F-04 is a high temperature, general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and p.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
Topas Advanced Polymers TOPAS® 9506F-500 Cyclic Olefin Copolymer (COC) TOPAS® 9506F-500 is a high clarity extrusion grade for use in shrink, food and medical packaging as either a discrete layer in multilayer film or in blends with polyethylene. It is designed to del.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
Topas Advanced Polymers TOPAS® 8007F-400 Cyclic Olefin Copolymer (COC) TOPAS® 8007F-400 is a robust film extrusion grade designed for blending with polyethylene (PE). It is a moderate clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, .. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
Total PPR 6280 Random Copolymer Polypropylene, Cast Film Extrusion Grade Total Petrochemicals PPR 6280 is a random copolymer polypropylene with a melt flow index of 7 g/10 min suitable for the cast extrusion of films with outstanding optical properties and easy heat weld.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | Blown Film at 1 mil; ASTM D-882 |
Chevron Phillips MarFlex® 7308DK Polyethylene; LLDPE Hexene linear low density polyethylene. This LLDPE is tailored for blown film applications that require: Excellent processingIncreased stiffnessGood toughnessUse alone or in blends with LDPE or HD.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | Blown Film at 1 mil; ASTM D-882 |
Chevron Phillips MarFlex® 7308DL Polyethylene; LLDPE Hexene linear low density polyethylene. This LLDPE is tailored for blown film applications that require: Excellent processingIncreased stiffnessGood toughnessUse alone or in blends with LDPE or HD.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | Blown Film at 1 mil; ASTM D-882 |
Chevron Phillips MarFlex® 7308FK Polyethylene; LLDPE Hexene linear low density polyethylene. This LLDPE is tailored for blown film applications that require: Excellent processabilityIncreased stiffnessGood toughnessUse alone or in blends with LDPE o.. |
|||
Film Tensile Strength at Break, MD | >= 55.0 MPa | >= 7980 psi | 55 N/10mm |
Dr. D. Mueller Flexiso® DMD FI 14010 00100 Polyester Electrical Insulation Structure: Flexiso® DMD, FI 14010 00100 is a flexible three layer material, consisting of a layer of polyester film, of which both sides have a layer of polyester fleece fabric and is coated with .. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ASTM D882 |
Dow AFFINITY™ PL 1840 Polyolefin Plastomer AFFINITY® PL 1840 polyolefin plastomer is an ethylene alpha-olefin resin designed to provide blown film products with low temperature sealability, excellent puncture resistance, outstanding blown f.. |
|||
Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | ISO 527-3 |
Polimeri Europa Eraclene® FA 506 Hexene Copolymer High Density Polyethylene - Blown Film Extrusion Eraclene FA 506 is a high density polyethylene resin (HDPE), hexene copolymer, with antioxidants, suitable for blown film extrusion.Its broad molecular weight distribution and density successfully c.. |