Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 193 - 276 MPa | 28000 - 40000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 1200MT Bi-Axially Oriented Nylon Film Description: Capran® Emblem™ 1200MT is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hy.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882 |
Total PPH 3270 Polypropylene Homopolymer, High Crystallinity, Low Melt Flow Film Grade Low Residuals TOTAL Polypropylene 3270 utilizes the TOTAL Polypropylene proprietary process technology to provide extremely low residuals for improved color stability and clarity.Slip/Antiblock. 3.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 314 Polyester Film, 92 Gauge Melinex® 314 is a two-side adhesion promoting polyester film with consistently good handling properties.Information provided by DuPont. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 453 Polyester Film, 300 Gauge Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 453 Polyester Film, 500 Gauge Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 453 Polyester Film, 700 Gauge Melinex® 453 is an excellent handling, high clarity film with one side pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 453 is used as a.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 454 Polyester Film, 200 Gauge Melinex® 454 is an excellent handling, high clarity film with both sides pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 454 is used as.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 454 Polyester Film, 500 Gauge Melinex® 454 is an excellent handling, high clarity film with both sides pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 454 is used as.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 454 Polyester Film, 700 Gauge Melinex® 454 is an excellent handling, high clarity film with both sides pre-treated to promote adhesion to most printing inks and Industrial coatings.Typical Applications: Melinex® 454 is used as.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 456 Polyester Film Melinex® 456 is an excellent handling, high clarity polyester film with both sides pretreated for slip. The two smooth surfaces allow easy top coating.Approvals: UL 94 VTM-2 - for 200 - 700 gauge (.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 581 Polyester Film A super clear, one side C-Sub pretreated film for adhesion of hydrophilic coatings.Approvals: UL Recognition - Product has been registered with Underwriters LaboratoriesInformation provided by DuPon.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 582 Polyester Film, 400 Gauge Melinex® 582 is a high clarity polyester film which is two-side hydrophilic pretreated to promote adhesion to many industrial aqueous coating and inks.Approvals: UL Recognition - Product has been r.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® SWC Polyester Film, 200 Gauge A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® SWC Polyester Film, 300 Gauge A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® SWC Polyester Film, 400 Gauge A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® SWC Polyester Film, 92 Gauge A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provi.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® A Polyester Film, 142 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, .. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® A Polyester Film, 200 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, .. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® A Polyester Film, 75 Gauge Mylar® A films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion, .. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® AHS1 Polyester Film, 92 Gauge Mylar® AHS1 is a strong, tough, and durable PET film with an unusual balance of properties. It is used for many industrial and electrical applications. General Product Info: Mylar® ASH1 has a tens.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® HR951 Polyester Film, 140 Gauge Mylar® HR951 is a one-side release coated polyester film with good handling properties and clarity. It has been developed for use in various industrial applications.Information provided by DuPont. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® RSX951 Polyester Film, 92 Gauge Mylar® RSX951 is a silicone coated polyester film designed for use as a release liner in various casting applications. The silicone release coating is applied to the film during the film production.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC11/WC22 Polyester Film, 284 Gauge Mylar® type WC11 films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectric and good handlin.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | 50% strain rate; ASTM D882A |
DuPont Teijin Films Melinex® 542 Polyester Film Melinex® 542 is a slightly hazy film with an adhesion promoting pretreatment on both sidesGeneral Product Info: The pretreatment enables numerous solvent and UV inks and lacquers to be coated with .. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 6428 Polyester Film, 200 Gauge Melinex® 6428 is a high clarity polyester film. It is pretreated on both film surfaces to promote adhesion to EVA. Melinex® 6428 is a developmental film designed for the photovoltaics industry.Als.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® D804 Polyester Film, 60 Gauge Mylar® D804 is a super clear, biaxially oriented, co-extruded polyester film, available in 60, 75 and 92 gauge. Mylar® D804 is two-side pretreated for printing and adhesive lamination. Approvals: .. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® MDA Polyester Film, 142 Gauge Mylar® MDA films are tough, general purpose films that are transparent in 48 through 92 gauge and translucent in heavier gauges. They have a rough surface to provide ease of handling, good adhesion.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC Polyester Film, 200 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Mylar® WC Polyester Film, 75 Gauge Mylar® WC films are general-purpose electrical grade films, similar to Mylar® EL. These clear to hazy films are tough and durable as a core wrap. They offer good dielectrics and good handling char.. |
|||
Film Tensile Strength at Break, MD | 193 MPa | 28000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 516R Polyester Film A high clarity film which is two side pretreated for slip to combine good handling properties with high clarity and brillianceInformation provided by DuPont. |