Polymer Property : Film Tensile Strength at Break, MD = 24900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	172 MPa	24900 psi	Orientation not specified; ASTM D882
DuPont™ Kapton® 50HN Polyimide Film, 13 Micron Thickness Film thickness 13 micron (0.5 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Available in thicknesses from 0.3 mil (7.5 µm) to 5 mil (125 µm).General..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	Orientation not specified; ASTM D882
DuPont™ Kapton® 50ZT Polyimide Film, 13 Micron Thickness Film thickness 13 micron (0.5 mil)All purpose polyimide film. Can be laminated, diecut, slit, formed, or adhesive-coated. Similar to Kapton® Type VN and HN with superior bondability. Available i..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	50% RH; Strain rate 50%/min; ASTM D882A
DuPont Teijin Films Melinex® 377 Polyester Film, 142 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	50% RH; Strain rate 50%/min; ASTM D882A
DuPont Teijin Films Melinex® 377 Polyester Film, 200 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	50% RH; Strain rate 50%/min; ASTM D882A
DuPont Teijin Films Melinex® 377 Polyester Film, 48 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	50% RH; Strain rate 50%/min; ASTM D882A
DuPont Teijin Films Melinex® 377 Polyester Film, 500 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	50% RH; Strain rate 50%/min; ASTM D882A
DuPont Teijin Films Melinex® 377 Polyester Film, 92 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® HS Polyester Film, 48 Gauge (12 µm) Data provided by DuPont Packaging Polymers.An uncoated, transparent polyester packaging film designed for heat shrink applications. It is currently available in 48, 65, 80, and 150 gauges, and othe..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® M34 Polyester Film, 75 Gauge (20 µm), PVDC Coated Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, solvent coated on one side with a PVDC copolymer. The coating is heat sealable, and is an excellent moisture and o..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® MC2 Polyester Film, 100 Gauge (25 µm), PVDC Coated Data provided by DuPont Packaging Polymers.A polyester film with a vacuum deposited layer of aluminum on one side and overcoated on both sides with a heat sealable PVDC copolymer. The film has exce..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB01 (formerly known as XM924) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and a polyvinylidene chlor..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the oppo..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the op..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL12 (formerly known as XM963A) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sea..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL12 (formerly known as XM963A) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sea..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL13 (formerly known as XM110) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat seal..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL33 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL33 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL4 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL4 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB01 (formerly known as XM924) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and a polyvinylidene chlor..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the oppo..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB12 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the oppo..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® LBT-2 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® LBT-2 is an uncoated, transparent, exceptionally strong film used as a substrate for laminating and extrusion coating and as a component of packagi..