- Polymer Property : Film Tensile Strength at Break, MD = 20300 psi
Polymer Property : Film Tensile Strength at Break, MD = 20300 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD11 Normal Grade Heat Sealable Film (thickness: 18 µm) HSD11 is a general, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent flatness and machinability, and good heat seal strength and dim.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD11 Normal Grade Heat Sealable Film (thickness: 20 µm) HSD11 is a general, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent flatness and machinability, and good heat seal strength and dim.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD11 Normal Grade Heat Sealable Film (thickness: 25 µm) HSD11 is a general, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent flatness and machinability, and good heat seal strength and dim.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD11 Normal Grade Heat Sealable Film (thickness: 30 µm) HSD11 is a general, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent flatness and machinability, and good heat seal strength and dim.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD12 Normal Grade Heat Sealable Film (thickness: 18 µm) HSD12 is a printing, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has corona trea.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD12 Normal Grade Heat Sealable Film (thickness: 20 µm) HSD12 is a printing, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has corona trea.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD13 Normal Grade Heat Sealable Film (thickness: 18 µm) HSD13 is a metalizing, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One side has co.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSD13 Normal Grade Heat Sealable Film (thickness: 20 µm) HSD13 is a metalizing, normal grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One side has co.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSS11 Normal Grade Heat Sealable Film (thickness: 30 µm) HSS11 is a general, normal grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent flatness and machinability, and good heat seal strength and dimens.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSS12 Normal Grade Heat Sealable Film (thickness: 18 µm) HSS12 is a printing, normal grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has corona treatme.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSS12 Normal Grade Heat Sealable Film (thickness: 30 µm) HSS12 is a printing, normal grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has corona treatme.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSS13 Normal Grade Heat Sealable Film (thickness: 18 µm) HSS13 is a metalizing, normal grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSS13 Normal Grade Heat Sealable Film (thickness: 20 µm) HSS13 is a metalizing, normal grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSS13 Normal Grade Heat Sealable Film (thickness: 25 µm) HSS13 is a metalizing, normal grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead HSS13 Normal Grade Heat Sealable Film (thickness: 30 µm) HSS13 is a metalizing, normal grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSD11 Low Temperature Grade Heat Sealable Film (thickness: 18 µm) LSD11 is a general, low temperature grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent flatness, and good heat seal strength. One side has co.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSD11 Low Temperature Grade Heat Sealable Film (thickness: 25 µm) LSD11 is a general, low temperature grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent flatness, and good heat seal strength. One side has co.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSD12 Low Temperature Grade Heat Sealable Film (thickness: 18 µm) LSD12 is a printing, low temperature grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has co.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSD12 Low Temperature Grade Heat Sealable Film (thickness: 20 µm) LSD12 is a printing, low temperature grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has co.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSD13 Low Temperature Grade Heat Sealable Film (thickness: 18 µm) LSD13 is a metalizing, low temperature grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One si.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSD13 Low Temperature Grade Heat Sealable Film (thickness: 25 µm) LSD13 is a metalizing, low temperature grade heat sealable film. It is transparent, and both sides are heat sealable. It has low static, excellent metal adhesion, and good heat seal strength. One si.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSS11 Low Temperature Grade Heat Sealable Film (thickness: 20 µm) LSS11 is a general, low temperature grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent flatness, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSS11 Low Temperature Grade Heat Sealable Film (thickness: 25 µm) LSS11 is a general, low temperature grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, excellent flatness, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSS12 Low Temperature Grade Heat Sealable Film (thickness: 18 µm) LSS12 is a printing, low temperature grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSS12 Low Temperature Grade Heat Sealable Film (thickness: 20 µm) LSS12 is a printing, low temperature grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | ASTM-D882 |
| Kinlead LSS12 Low Temperature Grade Heat Sealable Film (thickness: 25 µm) LSS12 is a printing, low temperature grade heat sealable film. It is transparent, and one side is heat sealable. It has low static, good ink adhesion, and good heat seal strength. One side has coron.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 20MB400 OPP Film Product Description: Bicor 20MB400 is a one side treated, sealable coextruded OPP film. It is designed for use in laminations.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 25MB400 OPP Film Product Description: Heat seal coextruded biaxially oriented polypropylene film that can be used on a wide range of packaging machines. 25MB400 can be either used as mono material or in laminated st.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 30MB400 OPP Film Product Description: A heat sealable coextruded biaxially oriented polypropylene film that can be used on a wide range of packaging machines. 30MB400 can be either used as mono material or in lamina.. |
|||
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| ExxonMobil Bicor™ 17MB400 OPP Film Product Description: Bicor 17MB400 is one side treated, sealable coextruded OPP film. It is designed for use in laminations.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Ou.. |
|||