Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 96.0 MPa | 13900 psi | parallel; ISO 527-3 |
DSM Akulon® F130-E1 PA6 Medium Viscosity, Nucleated, Lubricated, Film Extrusion |
|||
Film Tensile Strength at Break, MD | 96.0 MPa | 13900 psi | parallel; ISO 527-3 |
DSM Akulon® F130-E5 PA6 Medium Viscosity, Nucleated, Lubricated, Film Extrusion, Antiblock |
|||
Film Tensile Strength at Break, MD | 96.0 MPa | 13900 psi | parallel; ISO 527-3 |
DSM Akulon® F132-E1 PA6 Medium/High Viscosity, Nucleated, Lubricated, Film Extrusion |
|||
Film Tensile Strength at Break, MD | 96.0 MPa | 13900 psi | parallel; ISO 527-3 |
DSM Akulon® F132-E2 PA6 High Viscosity, Nucleated, Lubricated, Film Extrusion |
|||
Film Tensile Strength at Break, MD | 96.0 MPa | 13900 psi | parallel; ISO 527-3 |
DSM Akulon® XP32-E1 PA6 Film Extrusion, Medium Viscosity, Lubricated, Nucleated |
|||
Film Tensile Strength at Break, MD | 96.0 MPa | 13900 psi | parallel; ISO 527-3 |
DSM Akulon® XP36-E1 PA6 Film Extrusion, Medium Viscosity, Nucleated, Lubricated |