Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | supporting material; ASTM D882 |
Rogers Corporation Poron® 4701-15 Urethane Foam, Soft Seal PORON® 4701-15 Improved Soft Seal SeriesEnhanced Surface Toughness, Reliable Materials for Thinner DesignsIncreased Surface Toughness, Improved YieldsExcellent Compressibility and ConformabilityLon.. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | supporting material; ASTM D882 |
Rogers Corporation Poron® Shock Seal™ 4790-79-12 Handheld Urethane Foam, Handheld Grade, PET Reinforced Extreme Impact Protection, Ultimate ReliabilitySpecifically engineered to protect sensitive components from damage caused by impactConsistent cushioning performance through repeated impactsExcellent.. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | supporting material; ASTM D882 |
Rogers Corporation Poron® Shock Seal™ 4790-79-9 Handheld Urethane Foam, Handheld Grade, PET Reinforced Extreme Impact Protection, Ultimate ReliabilitySpecifically engineered to protect sensitive components from damage caused by impactConsistent cushioning performance through repeated impactsExcellent.. |
|||
Film Tensile Strength at Break, MD | 207 - 290 MPa | 30000 - 42000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 2530 Bi-Axially Oriented Nylon Film
(discontinued **) Description: Capran® Emblem™ 2530 is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbo.. |
|||
Film Tensile Strength at Break, MD | 207 - 290 MPa | 30000 - 42000 psi | ASTM D882 |
Honeywell Capran® Emblem™ 2500M M-Coated Bi-Axially Oriented Nylon Film Description: Capran® Emblem™ 2500M is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hyd.. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | Orientation not specified; ASTM D882 |
DuPont™ Kapton® 50KN Polyimide Film, 13 Micron Thickness Film thickness 13 micron (0.5 mil)Excellent processability, CTE close to copper, and a moderately high modulus.General Kapton® information: Kapton® is synthesized by polymerizing an aromatic dian.. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | ASTM D882A |
DuPont Teijin Films Melinex® 197 Polyester Film Melinex® 197 is a very clear polyester film with good handling properties, suitable for general purpose applications.Information provided by DuPont. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | ASTM D882A |
DuPont Teijin Films Melinex® D316 Polyester Film, 200 Gauge Melinex® D316 is a polyester film designed for the label industry, one side pretreated to promote adhesion to a wide variety of solventless, UV, EB, and thermal cured coatings.Adhesion promoting on.. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | JIS C-2318 (Modified to TDF) |
DuPont Teijin Films Teonex® Q83 Polyester Film, 200 Gauge Teonex® Q83 is biaxially oriented, slightly hazy polyethylene naphthalate (PEN) film with excellent handling properties and high dimensional stability. It is commercially available in 100, 200 and .. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | Orientation not specified; ASTM D882 |
DuPont™ Kapton® 120FN616 Polyimide/FEP Composite Film 120 Gauge film structure consisting of a 25 µm (1 mil) base polyimide film with a 2.5 µm (0.1 mil) coating of Teflon® FEP on both sides.Kapton® Type HN film coated with Teflon® FEP fluoropolyme.. |
|||
Film Tensile Strength at Break, MD | 207 MPa | 30000 psi | Average value: 207 MPa Grade Count:3 |
Overview of materials for Thermoset Polyurethane Foam, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane Foam, Unreinforced". Each property range of values reported is minimum and maximu.. |