Polymer Property : Film Tensile Strength at Break, MD = 172 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	172 MPa	24900 psi	50% RH; Strain rate 50%/min; ASTM D882A
DuPont Teijin Films Melinex® 377 Polyester Film, 142 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	50% RH; Strain rate 50%/min; ASTM D882A
DuPont Teijin Films Melinex® 377 Polyester Film, 75 Gauge Melinex® 377 is a translucent matte film having a medium surface gloss which is suitable for creating woodgrain and muted metallic effects.Typical Applications: Melinex® is suitable for use in sta..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 437 Polyester Film, 200 Gauge Melinex® 437 is a two side differentially pretreated super clear film; 1 side promotes adhesion, 1 side slip.Also available in 270, 370, 465, 650 GaugeInformation provided by DuPont.
Film Tensile Strength at Break, MD	>= 172 MPa	>= 25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 461 Polyester Film Melinex® 461 is a high clarity polyester film manufactured with a coating on one surface that promotes adhesion to many solvent formulations and to most vinyl or acrylic base ink systems. The adhes..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® 623 Polyester Film, 750 Gauge Melinex® 623 is a super clear polyester film pretreated on both surfaces to give superior solvent adhesion and improved handleability.Information provided by DuPont.
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Melinex® WCW Polyester Film, 75 Gauge Melinex® WCW is a translucent white polyester film with a rough surface for superior handling characteristics.Information provided by DuPont.
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® 851H Polyester Film, 60 Gauge Mylar® 851H (also called Mylar® 851) is a co-extruded, one side amorphous, heat sealable polyester film designed to be used in metallization, print, and lamination applications. This film is suita..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® HS Polyester Film, 48 Gauge (12 µm) Data provided by DuPont Packaging Polymers.An uncoated, transparent polyester packaging film designed for heat shrink applications. It is currently available in 48, 65, 80, and 150 gauges, and othe..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® M461 Polyester Film, 142 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® M461 Polyester Film, 48 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® M461 Polyester Film, 92 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® OB13AF Polyester Film, 100 Gauge Product Description: Mylar® OB13AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opposite s..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® OB13AF Polyester Film, 150 Gauge Product Description: Mylar® OB13AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opposite s..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL12 (formerly known as XM963A) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sea..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OL12 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL12 (formerly known as XM963A) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sea..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OL13 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OL13 (formerly known as XM110) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat seal..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® OL2 Polyester Film, 75 Gauge Product Description: Mylar® OL2 is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer. It is used as a heat sealable lidding film in packaging refrigerated and f..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® RB52 Polyester Film, 50 Gauge Product Description: Mylar® RB52 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer on one side and a polyvinylidene chloride (PVdC) layer on the opp..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® RL31 Polyester Film, 50 Gauge Mylar® RL31 is a biaxially oriented polyester (OPET) with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a heat sealable lidding film in packaging frozen and refrigerated foods. Myl..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL32 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL32 (formerly known as XM999) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL42 Polyester Packaging Film, 150 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL42 (formerly known as XM985) is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. It is used as a ..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® RL43 Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® RL43 is a biaxially oriented polyester (OPET) film with an ethylene vinyl acetate (EVA) heat seal layer. Mylar® RL43 is designed to produce stro..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX Polyester Film, 140 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® RSX Polyester Film, 300 Gauge Mylar® RSX films are slightly hazy, tough, general-purpose films. They have a rough surface to provide ease of handling, good adhesion, and processability. They are used for a broad range of indust..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® M461 Polyester Film, 300 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil..
Film Tensile Strength at Break, MD	172 MPa	25000 psi	ASTM D882A
DuPont Teijin Films Mylar® M461 Polyester Film, 400 Gauge Mylar® M461 is a tough, general purpose, untreated polyester film. It is transparent in 48 through 300 gauge and translucent in heavier gauges. Mylar® M461 is based on DuPont Teijin Film's RSX fil..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 50 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB01 (formerly known as XM924) is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and a polyvinylidene chlor..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® OB12AF Polyester Packaging Film, 100 Gauge Data provided by DuPont Packaging Polymers.Mylar® OB12AF is a biaxially oriented polyester (OPET) film with an amorphous polyester heat seal layer and polyvinylidene chloride (PVDC) layer on the op..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® M30 Polyester Film, 75 Gauge (21 µm), PVDC Coated (discontinued **) Data provided by DuPont Packaging Polymers.A transparent polyester packaging film, solvent coated on both sides with a PVDC copolymer. The coating is heat sealable, and is an excellent moisture and..
Film Tensile Strength at Break, MD	172 MPa	24900 psi	ASTM D882
DuPont Teijin Films Mylar® LBT-2 Polyester Packaging Film, 75 Gauge Data provided by DuPont Packaging Polymers.Mylar® LBT-2 is an uncoated, transparent, exceptionally strong film used as a substrate for laminating and extrusion coating and as a component of packagi..