Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | ASTM D882 |
SABIC F01552 High Density Polyethylene for Blown Film Product Description: F01552 is a high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weigh.. |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | ISO 527 |
Premix Thermoplastics PRE-ELEC® PE 1292 PRE-ELEC PE 1292 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 129.. |
|||
Film Tensile Strength at Yield, MD | 31.0 - 39.3 MPa | 4500 - 5700 psi | ASTM D882 |
Honeywell Halar® High Performance E-CTFE Film
(discontinued **) Description: Halar® is a high performance Ethylene-Chlorotrifluoroethylene (E-CTFE) film with excellent mechanical, electrical and release properties. It is non-flammable, and has outstanding chem.. |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | ASTM D882 |
LyondellBasell Alathon® L4907 High Density Polyethylene ApplicationsALATHON L 4907 is a high molecular weight high density copolymer with broad dimodal molecular weight distribution. This resin exhibits high density and stiffness and is designed for gro.. |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa @Thickness 0.0254 mm |
4500 psi @Thickness 0.00100 in |
ASTM D882A |
Total 9458 HDPE Film Grade Medium molecular weight grade. Excellent bubble stability, good compatibility with LDPE and LLDPE, good heat resistance, high stiffness and tensile strength.Applications: Release liners, Stand-up ba.. |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | ISO 527-3 |
Total PPH 4026 Polypropylene Homopolymer, Film Polypropylene PPH 4026 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.Polypropylene PPH 4026 is in.. |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | parallel; ISO 527-3 |
DSM Akulon® F130 PA6 Film Extrusion, Medium Viscosity |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | parallel; ISO 527-3 |
DSM Akulon® F130-C PA6 Film Extrusion, Medium Viscosity, Lubricated |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | parallel; ISO 527-3 |
DSM Akulon® F130-C2 PA6 Medium Viscosity, Film Extrusion, Lubricated |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | parallel; ISO 527-3 |
DSM Akulon® F130-C3 PA6 Monofilament Grade, Extrusion Grade, Medium Viscosity, Lubricated |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | parallel; ISO 527-3 |
DSM Akulon® F136 PA6 Very High Viscosity, Film Extrusion |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | parallel; ISO 527-3 |
DSM Akulon® F136-C PA6 Film Extrusion, Very High Viscosity, Lubricated |
|||
Film Tensile Strength at Yield, MD | 31.0 MPa | 4500 psi | parallel; ISO 527-3 |
DSM Akulon® F136-C1 PA6 Very High Viscosity, Film Extrusion, Lubricated |
|||
Film Tensile Strength at Yield, MD | 31.0 - 51.0 MPa | 4500 - 7400 psi | Average value: 36.8 MPa Grade Count:12 |
Overview of materials for Nylon 6, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Film Grade". Each property range of values reported is minimum and maximum values of appropriat.. |