Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | 4:1 safety factor; QTM 55010 |
Quadrant EPP Duratron® PAI T4203 Extruded Polyamide-imide (ASTM Product Data Sheet) |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | at 1 m/s unlubricated |
Quadrant EPP Ketron® HPV PEEK + carbon fibres + PTFE + graphite, bearing grade, extruded (ISO Data) The addition of carbon fibres, PTFE and graphite to virgin PEEK results in a Ketron PEEK “bearing grade”. Its excellent tribological properties (low friction, long wear and high pressure-velocity .. |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | (with 4:1 safety factor applied); QTM 55007 |
Quadrant EPP KETRON® MD PEEK, A Metal-Detectable Polyetheretherketone |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | at 1 m/s unlubricated |
Quadrant EPP Ketron® TX PEEK + solid lubricant, extruded (ISO Data) This member of the Ketron PEEK family has been developed especially for the food industry. Like Ketron PEEK-1000, this new internally lubricated material has a food contact compliant composition, bu.. |
|||
Limiting Pressure Velocity | 0.420 - 1.23 MPa-m/sec | 12000 - 35000 psi-ft/min | Average value: 0.812 MPa-m/sec Grade Count:4 |
Overview of materials for Polyetheretherketone, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Carbon Fiber Filled". Each property range of values reported is minimum and maximu.. |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | 4:1 safety factor; QTM 55007 |
Quadrant EPP Semitron® ESd 410C- CM Dissipative Polyetherimide(ASTM Product Data Sheet) |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | at 100 FPM, ambient temperature, thrust washer. |
Techmer ES Plaslube® AC-80/TF/15 Acetal (Copolymer), 15% PTFE Plaslube polytetrafluoroethylene (PTFE) lubricated acetal copolymer grades offer additional wear and friction performance over neat acetal. Typical applications include bearings, slides and small g.. |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | at 100 FPM, ambient temperature, thrust washer. |
Techmer ES Plaslube® J-1/30/SI/2 Nylon 66, 30% GFR, 2% Silicone Plaslube silicone lubricated nylon 66 grades are cost-effective wear and friction materials with low coefficients of friction. These grades have a potential for noise reduction due to the migratory.. |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | at 100 FPM, ambient temperature, thrust washer. |
Techmer ES Plaslube® NY-1/TF/10 Nylon 66, 10% PTFE Plaslube polytetrafluoroethylene (PTFE) lubricated nylon 66 grades offer the best wear and friction properties of any unreinforced, lubricated nylon compounds, making them ideal materials for bearin.. |
|||
Limiting Pressure Velocity | 0.420 MPa-m/sec | 12000 psi-ft/min | 10 fpm |
Ensinger Tecaform™ HPV 13 Acetal Homopolymer - Extruded Products (POM) Tecaform™ HPV 13 is a brown homopolymer acetal with an internal PTFE lubricant. Its low coefficient of friction, excellent PV values, toughness, wear resistance, and machinability make it an excep.. |
|||
Limiting Pressure Velocity | 0.420 - 0.440 MPa-m/sec | 12000 - 12600 psi-ft/min | Average value: 0.433 MPa-m/sec Grade Count:3 |
Overview of materials for Acetal Copolymer, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, PTFE Filled". Each property range of values reported is minimum and maximum values of .. |