Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 614 MPa @Temperature -53.9 °C |
89000 psi @Temperature -65.0 °F |
0° Direction, Dry; Vacuum/Oven Cured; ASTM D3039-95 |
Park Electrochemical Nelcote® E-765 Epoxy Prepreg, T300 6K 5HS Reinforced Nelcote® E-765 is a tough 250°F cure prepreg system designed to replace 350°F cure systems in aircraft structural applications. FAA-approved Design Allowable Databases are available upon request... |
|||
Tensile Strength, Yield | 614 MPa @Thickness 25.4 mm |
89000 psi @Thickness 1.00 in |
LT Direction |
Alcoa 7055-T7751 Aluminum Plate Alcoa introduced alloy 7055 in the -T7751 temper for plate and the -T77511 for extrusions in 1991. This alloy was developed for use in compression-dominated structures (such as upper wing structures.. |
|||
Tensile Strength, Yield | 614 MPa @Thickness 25.4 mm |
89000 psi @Thickness 1.00 in |
Longitudinal Direction |
Alcoa 7055-T77511 Aluminum Extrusions Alcoa introduced alloy 7055 in the -T7751 temper for plate and the -T77511 for extrusions in 1991. This alloy was developed for use in compression-dominated structures (such as upper wing structures.. |
|||
Tensile Strength, Yield | 614 MPa @Thickness 25.4 mm |
89000 psi @Thickness 1.00 in |
LT Direction |
Alcoa 7055-T77511 Aluminum Extrusions Alcoa introduced alloy 7055 in the -T7751 temper for plate and the -T77511 for extrusions in 1991. This alloy was developed for use in compression-dominated structures (such as upper wing structures.. |