Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 336 MPa @Thickness 6.30 mm, Temperature 20.0 °C |
48700 psi @Thickness 0.248 in, Temperature 68.0 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Tensile Strength, Yield | 336 MPa @Thickness 9.50 mm, Temperature 20.0 °C |
48700 psi @Thickness 0.374 in, Temperature 68.0 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Tensile Strength, Yield | 336 MPa @Diameter 12.7 mm, Temperature 260 °C |
48700 psi @Diameter 0.500 in, Temperature 500 °F |
0.2% Offset |
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process” phosphoric acid, which is widely used in the production of fertilizers. Tests indicate that it is.. |