Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 260 MPa @Strain 0.200 % |
37700 psi @Strain 0.200 % |
EN min.,RT; EN 10002-1 |
Outokumpu 4016 Ferritic Stainless Steel Fairly good corrosion resistant formable steel in mildly corrosive environments. Oxidation resistant at elevated temperatures (up to ~800°C). Ductile, does not work harden readily, and is well su.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 % |
37700 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 4550 Austenitic Stainless Steel Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto) and rod forms. |
|||
Tensile Strength, Yield | >= 260 MPa @Temperature 260 °C |
>= 37700 psi @Temperature 500 °F |
|
PEAK Werkstoff DISPAL S232 Aluminum Alloy, AlSi17Fe4Cu3Mg, Condition T6x Heat Treatment Condition T6x (Quench in water at RT). Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials all.. |
|||
Tensile Strength, Yield | >= 260 MPa @Temperature 150 °C |
>= 37700 psi @Temperature 302 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
Tensile Strength, Yield | 260 MPa @Temperature -10.0 °C |
37700 psi @Temperature 14.0 °F |
ASTM D638 |
Gharda Chemicals G-PAEKâ„¢ 1230CF Ultra High Performance PEK Polymer Product Details: Ultra High Performance Thermoplastic material, 30% carbon fiber reinforced in Poly Aryl Ether Ketone, semi-crystalline granules suitable for injection molding, easy flow, Black in .. |
|||
Tensile Strength, Yield | >= 260 MPa @Strain 1.00 % |
>= 37700 psi @Strain 1.00 % |
|
Industeel CLC 17.12.2 L 2% Mo Containing 18 Cr –10 Ni Austenitic Stainless Steel Description: CLC 17-12-2L is one of the basic grade of the stainless steels range. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform .. |
|||
Tensile Strength, Yield | >= 260 MPa @Strain 1.00 % |
>= 37700 psi @Strain 1.00 % |
|
Industeel CLC 17.12.2 Ti Titanium Stabilized 18Cr-11Ni-2Mo Austenitic Stainless Steel CLC 17-12-2Ti is a Titanium stabilized austenitic stainless steel. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform and localized co.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 1.00 % |
37700 psi @Strain 1.00 % |
Typical after Solution Annealing |
Industeel SIRIUS 309 23% Cr - 13% Ni Heat Resistant Stainless Steel Description: CLI SIRIUS 309 grade is a fully austenitic stainless steel containing 23% Cr, and 13% Ni additions. The alloy is well known for its multi-purpose high temperature corrosion resistance b.. |
|||
Tensile Strength, Yield | 259.9 MPa @Thickness 1.60 - 4.70 mm, Temperature 316 °C |
37700 psi @Thickness 0.0630 - 0.185 in, Temperature 601 °F |
0.2% offset |
Haynes Hastelloy® C-276 alloy, solution heat treated flat products Hastelloy® C-276 alloy is a nickel-molybdenum-chromium wrought alloy that is a versatile corrosion-resistant alloy. C-276 alloy is an improved wrought version of alloy C in that it usually doesn'.. |
|||
Tensile Strength, Yield | 260 - 320 MPa @Strain 0.200 % |
37700 - 46400 psi @Strain 0.200 % |
|
SSAB Tunnplat Docol® 260 BH High-strength Steel High-strength SteelComments: Docol BH - Cold Rolled Steel - rephosphorized steel with bake hardening effect. Property values are for cold-rolled steel; thicknesses 0.40 - 2.0 mm. Iron content is ap.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 % |
37700 psi @Strain 0.200 % |
as cast |
Wieland Eco E4 Casting Alloy Silver-palladium casting alloyApplications: crowns, short span bridges, long span bridgesDental |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 % |
37700 psi @Strain 0.200 % |
hardened |
Wieland Eco E4 Casting Alloy Silver-palladium casting alloyApplications: crowns, short span bridges, long span bridgesDental |
|||
Tensile Strength, Yield | >= 260 MPa @Strain 0.200 %, Thickness 7.90 - 12.5 mm |
>= 37700 psi @Strain 0.200 %, Thickness 0.311 - 0.492 in |
Temper T451; Standard EN 485-2 |
Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 2017A precision plates combine a very good dimensional stability with a high level of mechanical strength and elongation. The outstanding flatness, the low roughness and high quality of the.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 %, Thickness 8.00 - 25.0 mm |
37700 psi @Strain 0.200 %, Thickness 0.315 - 0.984 in |
Typical Strength |
Constellium DOKIMA® Rolled Plate Aluminum DOKIMA® rolled plates have moderate strength properties, a very low level of impurities, an excellent corrosion resistance, a very good dimensional stability and high thermal and electrical conduct.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 %, Thickness 25.0 - 60.0 mm |
37700 psi @Strain 0.200 %, Thickness 0.984 - 2.36 in |
Typical Strength |
Constellium DOKIMA® Rolled Plate Aluminum DOKIMA® rolled plates have moderate strength properties, a very low level of impurities, an excellent corrosion resistance, a very good dimensional stability and high thermal and electrical conduct.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 %, Thickness 60.0 - 100 mm |
37700 psi @Strain 0.200 %, Thickness 2.36 - 3.94 in |
Typical Strength |
Constellium DOKIMA® Rolled Plate Aluminum DOKIMA® rolled plates have moderate strength properties, a very low level of impurities, an excellent corrosion resistance, a very good dimensional stability and high thermal and electrical conduct.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 %, Thickness 100 - 150 mm |
37700 psi @Strain 0.200 %, Thickness 3.94 - 5.91 in |
Typical Strength |
Constellium DOKIMA® Rolled Plate Aluminum DOKIMA® rolled plates have moderate strength properties, a very low level of impurities, an excellent corrosion resistance, a very good dimensional stability and high thermal and electrical conduct.. |
|||
Tensile Strength, Yield | >= 260 MPa @Strain 0.200 %, Thickness 4.00 - 6.00 mm |
>= 37700 psi @Strain 0.200 %, Thickness 0.157 - 0.236 in |
Temper T651; Standard EN 485-2 |
Constellium PLAN 6082 Aluminum Rolled Plate Rolled plates in 6082 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6082 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
Tensile Strength, Yield | >= 260 MPa @Strain 0.200 %, Thickness 4.99 - 6.00 mm |
>= 37700 psi @Strain 0.200 %, Thickness 0.196 - 0.236 in |
Temper T651; Standard EN 485-2 |
Constellium Planoxal® 60 Aluminum plate The advantage of Planoxal®-60 plates over other standard EN AW-6082 alloy products is their low level of internal stress. They are also suitable for technical anodizing. Planoxal®-60 is mainly use.. |
|||
Tensile Strength, Yield | 260 MPa @Thickness 3.20 mm, Temperature 760 °C |
37700 psi @Thickness 0.126 in, Temperature 1400 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 % |
37700 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 904L High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
Tensile Strength, Yield | >= 260 MPa @Strain 1.00 % |
>= 37700 psi @Strain 1.00 % |
|
Industeel URANUS® S1 4 % Si, Austenitic Stainless Steel Resistant to Nitric Acid Solutions Description: Research carried out in about the last fifteen years in CREUSOT LOIRE INDUSTRIE laboratories shows that a strong addition of silicon to austenitic stainless steels of the 18/10 type has.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 % |
37700 psi @Strain 0.200 % |
Typical after Solution Annealing |
Industeel UREA 25.22.2 Plants Description: CLI UREA 25.22.2 chemical composition has been optimized for specific uses in Urea plants. It is a 310L modified austenitic stainless steel with low carbon, low silicon and high nitroge.. |
|||
Tensile Strength, Yield | 260 MPa @Strain 0.200 %, Temperature 260 °C |
37700 psi @Strain 0.200 %, Temperature 500 °F |
|
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |