Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 255 MPa @Strain 0.200 % |
37000 psi @Strain 0.200 % |
|
PSM Industries PolyAlloys MIM-2700 sintered Low Alloy Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
Tensile Strength, Yield | 255 MPa @Thickness 3.17 mm |
37000 psi @Thickness 0.125 in |
CW |
Industrial Laminates/Norplex MC514MG Glass Fabric Description: MC514MG is made with a woven glass fabric in combination with high temperature, conductive, phenolic resin system.NP514MG has excellent flexural, compressive and impact strengths at roo.. |
|||
Tensile Strength, Yield | 255 MPa @Thickness 1.57 mm |
37000 psi @Thickness 0.0620 in |
CW; ASTM D638 |
Industrial Laminates/Norplex NP511 Glass Fabric Description: Woven glass fabric with high temperature epoxy resin. Excellent mechanical strength and electrical properties at elevated temperatures. Continuous operating temperature is 165°C. Mat.. |
|||
Tensile Strength, Yield | 255 MPa @Strain 0.200 %, Temperature 400 °C |
37000 psi @Strain 0.200 %, Temperature 752 °F |
|
Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Tensile Strength, Yield | 255 MPa @Thickness 6.30 mm, Temperature 427 °C |
37000 psi @Thickness 0.248 in, Temperature 801 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, plate, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) rang.. |
|||
Tensile Strength, Yield | >= 255 MPa @Strain 0.200 %, Thickness 6.00 - 12.5 mm |
>= 37000 psi @Strain 0.200 %, Thickness 0.236 - 0.492 in |
Temper T651; Standard EN 485-2 |
Constellium PLAN 6082 Aluminum Rolled Plate Rolled plates in 6082 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6082 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
Tensile Strength, Yield | >= 255 MPa @Strain 0.200 %, Thickness 6.00 - 12.0 mm |
>= 37000 psi @Strain 0.200 %, Thickness 0.236 - 0.472 in |
Temper T651; Standard EN 485-2 |
Constellium Planoxal® 60 Aluminum plate The advantage of Planoxal®-60 plates over other standard EN AW-6082 alloy products is their low level of internal stress. They are also suitable for technical anodizing. Planoxal®-60 is mainly use.. |
|||
Tensile Strength, Yield | >= 255 MPa @Strain 0.200 %, Thickness 9.90 - 12.5 mm |
>= 37000 psi @Strain 0.200 %, Thickness 0.390 - 0.492 in |
Temper T651; Standard EN 485-2 |
Constellium ALPLAN® 6082 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6082 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
Tensile Strength, Yield | 255 MPa @Temperature 23.0 °C |
37000 psi @Temperature 73.4 °F |
|
Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled One of the most characteristic properties of polyamide (PA 6.6) is the absorption of moisture. This essentially leads to increased toughness and elongation at break, to name the most important param.. |
|||
Tensile Strength, Yield | 255 MPa @Strain 0.200 %, Thickness 38.13 - 76.2 mm |
37000 psi @Strain 0.200 %, Thickness 1.501 - 3.00 in |
Rolled Plate |
Magnesium Elektron Elektron® 43 Magnesium Wrought Alloy High strength wrought Mg alloy available as rolled plate, forging feedstock, and extrusions. It is a wrought evolution of the casting alloy Elektron WE43. Elektron 43 uses zirconium grain refining.. |
|||
Tensile Strength, Yield | 255 MPa @Thickness 9.50 mm, Temperature 316 °C |
37000 psi @Thickness 0.374 in, Temperature 601 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |