Polymer Property : Tensile Strength, Yield = 20300 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Temperature 400 °C	20300 psi @Strain 0.200 %, Temperature 752 °F	EN min.; EN 10002-5
Outokumpu 153MA™ High Temperature Austenitic Stainless Steel Variant of 1.4301 with increased silicon and nitrogen contents and microalloyed with rare earth metals (REM). This raises the max service temperature in dry air to 1000°C.Applications: Heat and cr..
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Temperature 600 °C	20300 psi @Strain 0.200 %, Temperature 1110 °F	EN min.; EN 10002-5
Outokumpu 253MA® High Temperature Austenitic Stainless Steel Variant of 1.4828 with increased nitrogen content and has been microalloyed with rare earth metals (REM). The most suitable temperature range is 850-1100°C, because structural changes when used be..
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Temperature 100 °C	20300 psi @Strain 0.200 %, Temperature 212 °F	EN min.; EN 10002-5
Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Temperature 100 °C	20300 psi @Strain 0.200 %, Temperature 212 °F	EN min.; EN 10002-5
Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and ..
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Temperature 100 °C	20300 psi @Strain 0.200 %, Temperature 212 °F	EN min.; EN 10002-5
Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o..
Tensile Strength, Yield	140 MPa @Temperature -10.0 Â°C	20300 psi @Temperature 14.0 Â°F	ASTM D638
Gharda Chemicals G-PAEKâ„¢ 1200G Ultra High Performance PEK Polymer Product Details: Ultra High Performance Thermoplastic (Poly Aryl Ether Ketone) material, virgin semi-crystalline granules suitable for injection molding, easy flow, Beige in colorApplication Areas:..
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Thickness 20.0 - 150 mm	20300 psi @Strain 0.200 %, Thickness 0.787 - 5.91 in	Typical Strength
Constellium PLAN 5754 Aluminum Rolled Plate Rolled plates in 5754 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 5754 PLAN is mainly used for low stressed mechanical components, manufactured by intensive m..
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Thickness 20.0 - 150 mm	20300 psi @Strain 0.200 %, Thickness 0.787 - 5.91 in	Typical Strength
Constellium PLAN OX 5754 Aluminum Rolled Plate Rolled plates in 5754 PLAN OX are optimized for minimum residual stress, improved dimensional tolerances and for decorative* anodizing. 5754 PLAN OX is mainly used for low stressed, anodized compone..
Tensile Strength, Yield	140 MPa @Strain 0.200 %, Thickness 20.0 - 100 mm	20300 psi @Strain 0.200 %, Thickness 0.787 - 3.94 in	Typical Strength
Constellium Planoxal® 50 Aluminum plate Planoxal®-50 plates differ from other standard EN-AW 5083 alloy products by their low level of residual stress. This specialty plate is also suitable for decorative anodizing. Planoxal®-50 is main..