Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 138 MPa @Thickness 1.57 mm |
20000 psi @Thickness 0.0620 in |
LW; ASTM D638 |
Industrial Laminates/Norplex NP842 Paper Base Laminate
(discontinued **) Description: Paper reinforced phenolic grade with controlled conductivity. Mechanical strength similar to NP611. NP842 is semi-conductive on the surfaces and through the laminate.Thickness Tested: 0.. |
|||
Tensile Strength, Yield | 138 MPa @Thickness 1.57 mm |
20000 psi @Thickness 0.0620 in |
LW; ASTM D638 |
Industrial Laminates/Norplex NP610 Paper Base Laminate Description: Phenolic paper based grade for mechanical applications. Good tensile, compressive and flexural strength. Primarily a machining material, but may be hot punched up to .093" thick.Thickne.. |
|||
Tensile Strength, Yield | 138 MPa @Thickness 1.57 mm |
20000 psi @Thickness 0.0620 in |
LW; ASTM D638 |
Industrial Laminates/Norplex NP660 Paper Base Laminate Description: Lower cost paper phenolic NEMA Grade XP. Uses natural kraft paper without pigmented cover sheet. Warm to hot punching. UL listed. Thickness Tested: 0.062", 0.125" & 0.500" |
|||
Tensile Strength, Yield | 138 MPa @Diameter 25.4 mm |
20000 psi @Diameter 1.00 in |
Rod H02 |
Mueller Ecostream™ C36300 Copper Zinc Lead Alloy As one of the low lead alloys offered in the EcoStream™ family of products, Mueller Brass Company’s C36300 alloy provides a viable alternative to those manufacturers who are manufacturing .. |
|||
Tensile Strength, Yield | 138 MPa @Temperature 177 °C |
20000 psi @Temperature 351 °F |
[+/-45°]; Resin Content=27%, Fiber Volume=66% |
Hexcel® HexPly® F650 Bismaleimide Resin with IM6 Fiber Composition: IM6 Fiber, 12K, G sizes, UD Tape - 145 g/m2Information provided by HexCel |
|||
Tensile Strength, Yield | >= 138 MPa @Strain 0.200 %, Thickness <=63.5 mm |
>= 20000 psi @Strain 0.200 %, Thickness <=2.50 in |
|
Carlson 70 30 Cu Ni Copper-Nickel Alloy General DescriptionCarlson alloy 70 30 Cu Ni is a copper nickel alloy with excellent resistance to corrosion and erosion. It is strong and ductile. 70 30 Cu Ni is utilized in areas where high temp.. |
|||
Tensile Strength, Yield | 138 MPa @Temperature -40.0 °C |
20000 psi @Temperature -40.0 °F |
ASTM D638 |
BASF Ultramid® 8270 HS BK 102 PA6 (Dry) Description: Ultramid 8270 HS BK-102 is a thermally modified pigmented black, PA6 blow molding compound exhibiting exceptional toughness and melt strength ideally suited for blow molding, profile ex.. |
|||
Tensile Strength, Yield | 138 MPa @Temperature 760 °C |
20000 psi @Temperature 1400 °F |
ASTM E8 |
ATI Allegheny Ludlum 309 Austenitic Stainless Steel Characteristics: comparable corrosion resistance, superior resistance to oxidation, and the retention of a larger fraction of room temperature strength than common austenitic alloys. Good creep defo.. |
|||
Tensile Strength, Yield | 138 MPa @Temperature 1090 °C |
20000 psi @Temperature 2000 °F |
Vacuum |
ATI Wah Chang Nb/Nb Alloy C-103 This alloy satisfies most rocket engine applications for temperatures up to 2700°F because of superior mechanical properties at all temperatures. Offers weight savings over many rocket engine desig.. |
|||
Tensile Strength, Yield | >= 138 MPa @Strain 0.200 % |
>= 20000 psi @Strain 0.200 % |
|
PSM Industries PolyAlloys MIM-316L sintered Stainless Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |