Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 731 MPa @Strain 0.200 % |
106000 psi @Strain 0.200 % |
|
PSM Industries PolyAlloys MIM-17-4PH sintered Stainless Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
Tensile Strength, Yield | 730 MPa @Temperature 600.0 °C |
106000 psi @Temperature 1112 °F |
|
International Mold Steel DH2F Pre-Hardened H13-Type Mold Steel Description: DH2F is one of the best machining pre-hardened H13-type steels available.Unique Characteristics: 38-42 HRc hardness.Through hardened for exceptional dimensional stability.Cuts mold maki.. |
|||
Tensile Strength, Yield | 731 MPa @Strain 0.200 % |
106000 psi @Strain 0.200 % |
4 in. Test Specimen |
Latrobe Lescalloy® 410Cb High Strength Stainless Steel LESCALLOY 17-4 VAC-ARC steel is a precipitation hardening martensitic stainless steel. A wide range of mechanical properties is available via simple aging within a 900-1150°F (482-621°C) tempe.. |
|||
Tensile Strength, Yield | 733 MPa @Temperature 25.0 °C, Time 11500 sec |
106000 psi @Temperature 77.0 °F, Time 3.20 hour |
As Welded and Aged at 1850°F(1010°C)/2hr/AC + 1450°F(788°C)/8h/AC; Base/Weld Fracture; 0.2% Offset |
Haynes 282® Nickel Alloy Autogenously Welded Sheet Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |
|||
Tensile Strength, Yield | 731 MPa @Strain 2.00 %, Temperature 538 °C |
106000 psi @Strain 2.00 %, Temperature 1000 °F |
H900 |
Crucible Steel 15-5 Precipitation Hardening Stainless Steel Crucible 15-5 is a Premium Quality precipitation-hardening stainless steel which is capable of high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is a V.. |
|||
Tensile Strength, Yield | 731 MPa @Strain 2.00 %, Temperature 538 °C |
106000 psi @Strain 2.00 %, Temperature 1000 °F |
H900 |
Crucible Steel 17Cr-4Ni Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a precipitation-hardening stainless steel which is capable of a high strength and hardness levels after a relatively simple heat-treatment procedure. This grade is martensitic a.. |
|||
Tensile Strength, Yield | 731 MPa @Strain 2.00 %, Temperature 538 °C |
106000 psi @Strain 2.00 %, Temperature 1000 °F |
H900 |
Crucible Steel 17Cr-4Ni Super-X® Precipitation Hardening Stainless Steel Crucible 17Cr-4Ni is a version of 17CR-4Ni which has been modified to substantially improve machinability and other properties. Patented 17Cr-4Ni Super-X meets industry specifications for 17Cr-4Ni. .. |