Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | >= 72.0 MPa @Temperature 300 °C |
>= 10400 psi @Temperature 572 °F |
|
PEAK Werkstoff DISPAL S270 Aluminum Alloy, AlSi25Fe4Ni3CuMgMnCrTi, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
Tensile Strength, Yield | 71.7 MPa @Thickness 1.57 mm |
10400 psi @Thickness 0.0620 in |
CW; ASTM D638 |
Industrial Laminates/Norplex NP625 Paper Base Laminate Description: Paper phenolic grade with better moisture resistance than NP612. Requires less heat to punch and shear than NP611. |
|||
Tensile Strength, Yield | 72.0 MPa @Temperature 23.0 °C |
10400 psi @Temperature 73.4 °F |
90° |
Hexcel® HexPly® 954-6 Curing Cyanate Resin, M40J Fiber Information provided by HexCel |
|||
Tensile Strength, Yield | 72.0 MPa @Temperature 23.0 °C |
10400 psi @Temperature 73.4 °F |
5mm/min (0.2in/min); ASTM D638 |
DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and mod.. |
|||
Tensile Strength, Yield | 72.0 MPa @Temperature 23.0 °C |
10400 psi @Temperature 73.4 °F |
ISO 527 |
DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and mod.. |
|||
Tensile Strength, Yield | 72.0 MPa @Temperature 23.0 °C |
10400 psi @Temperature 73.4 °F |
ASTM D638 |
BASF Ultramid® 8281 HS GP PA6 (Dry) Description: Ultramid 8281 HS GP is an unreinforced, heat stabilized PA6 rot molding compound. It is available in natural and black and can be painted. It exhibits excellent balance of engineering p.. |