Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 831 MPa @Strain 0.200 %, Thickness 1.45 mm |
121000 psi @Strain 0.200 %, Thickness 0.0571 in |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Yield | 831 MPa @Temperature 25.0 °C, Time 45700 sec |
121000 psi @Temperature 77.0 °F, Time 12.7 hour |
As Welded and Aged at 1850°F(1010°C)/2hr/AC + 1450°F(788°C)/8h/AC; Weld/Weld Fracture; 0.2% Offset |
Haynes 282® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and la.. |