Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 455 MPa @Temperature 21.1 °C |
66000 psi @Temperature 70.0 °F |
0° Direction, Dry; ASTM D638 |
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 120 E-Glass Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle.. |
|||
Tensile Strength, Yield | 455 MPa @Diameter 12.7 mm |
66000 psi @Diameter 0.500 in |
As welded; 0.2% offset |
Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform Outstanding Corrosion Resistance, High Strength HASTELLOY® C-22HSTM alloy is corrosion-resistant, nickel-chromium-molybdenum alloy which can be heat treated to obtain a strength approximately dou.. |
|||
Tensile Strength, Yield | >= 455 MPa @Strain 0.200 %, Temperature 250 °C |
>= 66000 psi @Strain 0.200 %, Temperature 482 °F |
|
ThyssenKrupp N-A-XTRA® 550 Structural Steel This Material Specification applies to quenched and tempered heavy plates made of the special structural steel N-A-XTRA® This steel can be supplied in 3 different grades with a minimum yield streng.. |
|||
Tensile Strength, Yield | 455 MPa @Temperature 24.0 °C |
66000 psi @Temperature 75.2 °F |
|
Hexcel® F161 Epoxy Resin, 120 Glass Fabric Hexcel designation: 120-38"-F161; Fiber: 450-1/2Information provided by HexCel |
|||
Tensile Strength, Yield | 455 MPa @Thickness >=508 mm |
66000 psi @Thickness >=20.0 in |
at center (L/T direction) |
Alcoa QC-10® Aluminum Mold Alloy Specifically designed for high production injection and blow mold applications, QC-10 offers outstanding strength, stability, and durability. Its improved alloy composition provides outstanding, 1"-.. |
|||
Tensile Strength, Yield | >= 455 MPa @Strain 0.200 %, Thickness 203.2 - 254 mm |
>= 66000 psi @Strain 0.200 %, Thickness 8.000 - 10.0 in |
Tempers T651 / T652 |
Constellium Alumold® 500 Rolled Aluminum The Alumold® 500 alloy has been optimized to provide excellent machinability, good shape stability and high strength properties throughout the plate thickness. Uniform strength is an important prop.. |
|||
Tensile Strength, Yield | 455 MPa @Strain 0.200 %, Thickness 140 - 160 mm |
66000 psi @Strain 0.200 %, Thickness 5.51 - 6.30 in |
Typical Strength |
Constellium Fortal® Aluminum Alloy Fortal® plates are optimized to provide high mechanical strength, combined with good shape stability and excellent machinability. Typical applications include sheet forming tools, base plates for m.. |
|||
Tensile Strength, Yield | 455 MPa @Strain 0.200 % |
66000 psi @Strain 0.200 % |
Typical |
Aleris Hokotol Aluminum Alloy, 300 mm Thickness Sample treatment not specified for property data.Applications include molds for blow forming and injection molding for plastics; bolsters and force plates; high strength/low weight machine parts; an.. |
|||
Tensile Strength, Yield | >= 455 MPa @Thickness 3.17 mm |
>= 66000 psi @Thickness 0.125 in |
LT Direction |
Alcoa 2090-T83 Aluminum Aluminum-lithium alloy developed for high strength aerospace applications. The Al-Cu-Li alloy offers an 8 per cent density savings when compared with other aerospace alloys. Alloy 2090-T83 also has .. |
|||
Tensile Strength, Yield | 455 MPa @Temperature 149 °C |
66000 psi @Temperature 300 °F |
Annealed |
ATI Wah Chang TI-3Al-2.5V Ti-3Al-2.5V has proved to be a sufficiently malleable material for tube manufacture. It can be cold worked by standard tube making processes, is weldable and can be strength-ended by cold working an.. |