Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 331 MPa @Temperature 260 °C |
48000 psi @Temperature 500 °F |
0° Direction, Dry; 325°F Autoclave Cured; ASTM D638 |
Park Electrochemical Nelcote® F-502 Phenolic Prepreg, 7781 E-Glass Reinforced Nelcote® F-502 is a MIL-R-9299 phenolic resin system suitable for impregnation on any MIL-C-9084 fabric with a compatible finish. F-502 is used in the manufacture of ablative reinforcements in rock.. |
|||
Tensile Strength, Yield | 331 MPa @Thickness 1.57 mm |
48000 psi @Thickness 0.0620 in |
CW; ASTM D638 |
Industrial Laminates/Norplex NP511ES Glass Epoxy Laminate Description: NP511ES is a woven glass fabric with high temperature, static dissipative epoxy resin. It has excellent mechanical strength and electrical properties at elevated temperatures with a con.. |
|||
Tensile Strength, Yield | 331 MPa @Thickness 3.17 mm |
48000 psi @Thickness 0.125 in |
LW |
Industrial Laminates/Norplex P95 Glass Fabric Description: Woven glass fabric with polyimide resin engineered to maintain excellent physical properties at 240°C. Low coefficient of thermal expansion, high mechanical strength.Thickness Tested.. |
|||
Tensile Strength, Yield | 331 MPa @Thickness 9.50 - 25.4 mm, Temperature 204 °C |
48000 psi @Thickness 0.374 - 1.00 in, Temperature 399 °F |
0.2% offset |
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Yield | 331 MPa @Diameter 9.70 mm, Temperature 25.0 °C |
48000 psi @Diameter 0.382 in, Temperature 77.0 °F |
0.2% offset |
Haynes Hastelloy® C-2000® Bar, Annealed at 2100°F (1149°C) Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |