| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 310 MPa @Strain 0.200 % |
45000 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4439 Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), and cold rolled strip/sheet forms. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 %, Temperature 200 °C |
45000 psi @Strain 1.00 %, Temperature 392 °F |
EN min.; EN 10002-5 |
| Outokumpu 4565 High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Outokumpu Typical,Cold Rolled Strip/Sheet; EN 10002-1 |
| Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
| Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o.. |
|||
| Tensile Strength, Yield | 310 MPa @Temperature 216 °C |
45000 psi @Temperature 420 °F |
0° Direction, Dry; ASTM D638 |
| Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac.. |
|||
| Tensile Strength, Yield | 310 MPa @Temperature 260 °C |
45000 psi @Temperature 500 °F |
0° Direction, Dry; ASTM D638 |
| Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac.. |
|||
| Tensile Strength, Yield | 310 MPa @Temperature 216 °C |
45000 psi @Temperature 420 °F |
0° Direction, Dry, Autoclave; ASTM D638 |
| Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac.. |
|||
| Tensile Strength, Yield | 310 MPa @Temperature 260 °C |
45000 psi @Temperature 500 °F |
0° Direction, Dry, Autoclave; ASTM D638 |
| Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-746 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-746 has a proven history in many demanding aerospac.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 1.57 mm |
45000 psi @Thickness 0.0620 in |
LW; ASTM D638 |
| Industrial Laminates/Norplex NP130 Glass Fabric Description: Woven glass fabric combined with a halogenated epoxy resin system. Produced to printed circuit board quality standards. Flame retardant, meets UL-94 flammability classification V-0.Thic.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 % |
45000 psi @Strain 0.200 % |
Typical |
| Industeel CLC 17.12.2 L 2% Mo Containing 18 Cr –10 Ni Austenitic Stainless Steel Description: CLC 17-12-2L is one of the basic grade of the stainless steels range. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform .. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 1.00 % |
45000 psi @Strain 1.00 % |
Typical |
| Industeel CLC 17.12.2 Ti Titanium Stabilized 18Cr-11Ni-2Mo Austenitic Stainless Steel CLC 17-12-2Ti is a Titanium stabilized austenitic stainless steel. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform and localized co.. |
|||
| Tensile Strength, Yield | >= 310 MPa @Strain 1.00 % |
>= 45000 psi @Strain 1.00 % |
|
| Industeel CLC 18.10 LN Nitrogen Containing 18Cr-10Ni Austenitic Stainless Steel Description: CLC 18.10LN is a 18Cr-10Ni austenitic stainless steel with specific Nitrogen additions. Its low carbon content avoids intergranular corrosion, even on welded pieces without an ulterior .. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 19.0 mm, Temperature 538 °C |
45000 psi @Thickness 0.750 in, Temperature 1000 °F |
0.2% offset |
| Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 12.7 mm, Temperature 538 °C |
45000 psi @Thickness 0.500 in, Temperature 1000 °F |
0.2% offset |
| Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 12.7 mm, Temperature 260 °C |
45000 psi @Thickness 0.500 in, Temperature 500 °F |
0.2% Offset |
| Haynes Hastelloy® G-35® Nickel Alloy Gas Tungsten Arc Welded (GTAW) Plate Known for its corrosion performance, HASTELLOY® G-35® alloy was designed to resist “wet process†phosphoric acid, which is widely used in the production of fertilizers. Tests indicat.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Temperature 20.0 °C |
45000 psi @Strain 0.200 %, Temperature 68.0 °F |
|
| Magnesium Elektron Elektron® 675 Magnesium Wrought Alloy High strength wrought Mg alloy used for high performance components, including at elevated temperature. Excellent corrosion resistance and easily machined. Can be extruded, forged and hot formed. .. |
|||
| Tensile Strength, Yield | >= 310 MPa @Strain 0.200 %, Thickness 50.8 - 76.2 mm |
>= 45000 psi @Strain 0.200 %, Thickness 2.00 - 3.00 in |
Tempers T851/T852 |
| Constellium Alumold® 350 Aluminum Alumold-350® has been specifically developed to achieve the best combination of strength at low and high temperatures, together with a good shape stability and machinability. Alumold-350® is parti.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 254 - 305 mm |
45000 psi @Strain 0.200 %, Thickness 10.0 - 12.0 in |
Typical Strength |
| Constellium Alumold® 350 Aluminum Alumold-350® has been specifically developed to achieve the best combination of strength at low and high temperatures, together with a good shape stability and machinability. Alumold-350® is parti.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 25.0 - 60.0 mm |
45000 psi @Strain 0.200 %, Thickness 0.984 - 2.36 in |
Typical Strength; Standard EN 485-2 |
| Constellium PLAN 6082 Aluminum Rolled Plate Rolled plates in 6082 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6082 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 60.0 - 150 mm |
45000 psi @Strain 0.200 %, Thickness 2.36 - 5.91 in |
Typical Strength; Standard EN 485-2 |
| Constellium PLAN 6082 Aluminum Rolled Plate Rolled plates in 6082 PLAN are optimized for minimum residual stress and improved dimensional tolerances. 6082 PLAN is mainly used for medium stressed mechanical components, manufactured by intensiv.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 20.0 - 80.0 mm |
45000 psi @Strain 0.200 %, Thickness 0.787 - 3.15 in |
Typical Strength |
| Constellium Planoxal® 60 Aluminum plate The advantage of Planoxal®-60 plates over other standard EN AW-6082 alloy products is their low level of internal stress. They are also suitable for technical anodizing. Planoxal®-60 is mainly use.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 25.0 - 60.0 mm |
45000 psi @Strain 0.200 %, Thickness 0.984 - 2.36 in |
Typical Strength |
| Constellium ALPLAN® 6082 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6082 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
| Tensile Strength, Yield | 310 MPa @Strain 0.200 %, Thickness 60.0 - 140 mm |
45000 psi @Strain 0.200 %, Thickness 2.36 - 5.51 in |
Typical Strength |
| Constellium ALPLAN® 6082 Rolled Precision Aluminum Plate, Milled Both Sides Precision plates in ALPLAN® 6082 are milled on both sides and have a very low level of residual stress, thus avoiding excessive deformation during machining. Thanks to its very good dimensional sta.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 1.60 mm |
45000 psi @Thickness 0.0630 in |
LT Direction |
| Aleris AA5024-H116 Aluminum Magnesium Scandium Alloy Features good weldability, excellent damage tolerance, good corrosion resistance, creep-formability. Aleris AlMgSc alloy AA5024 H116 allows simplification of the manufacturing process of aircraft f.. |
|||
| Tensile Strength, Yield | 310 MPa @Thickness 12.7 mm, Temperature 538 °C |
45000 psi @Thickness 0.500 in, Temperature 1000 °F |
0.2% offset |
| Haynes Hastelloy® C-22® alloy, transverse, GTAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||