Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 250 MPa @Strain 1.00 % |
36300 psi @Strain 1.00 % |
EN min.,RT; EN 10002-1 |
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
Tensile Strength, Yield | 250 MPa @Strain 0.200 % |
36300 psi @Strain 0.200 % |
Outokumpu Typical,Cold Rolled Narrow Strip; EN 10002-1 |
Outokumpu 4303 Cr-Ni Austenitic Stainless Steel Good corrosion resistance with excellent drawing properties.Applications: Suitable for cold formed components where good workability is required. Fasteners, studs.Available in hot rolled plate (Qua.. |
|||
Tensile Strength, Yield | 250 MPa @Strain 0.200 % |
36300 psi @Strain 0.200 % |
EN min.,RT; EN 10002-1 |
Outokumpu 4310 Cr-Ni Austenitic Stainless Steel Cold work hardening steel suitable for manufacture of springs operating in corrosive conditions.Available hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and ro.. |
|||
Tensile Strength, Yield | 250 MPa @Strain 0.200 % |
36300 psi @Strain 0.200 % |
Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1 |
Outokumpu 4541 Cr-Ni Austenitic Stainless Steel Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (C.. |
|||
Tensile Strength, Yield | >= 250 MPa @Strain 1.00 % |
>= 36300 psi @Strain 1.00 % |
|
Industeel CLC 18.15.4L 3% Mo Minimum Austenitic Stainless Steel Description: CLC 18-15-4L (317L) is an austenitic stainless steel with a 3% minimum Molybdenum addition. Alloys CLC 18-15-4L (317L) exhibit austenitic microstructure free of deleterious carbide prec.. |
|||
Tensile Strength, Yield | >= 250 MPa @Strain 1.00 % |
>= 36300 psi @Strain 1.00 % |
|
Industeel URANUS® B28 High Nickel Super-Austenitic Stainless Steel Description: URANUS® B28 (UR B28) is a super-austenitic stainless steel with very high nickel (31%) and chromium (27%) contents. The molybdenum content is about 3.5%. The alloy is designed for sp.. |
|||
Tensile Strength, Yield | >= 250 MPa @Strain 0.200 %, Thickness 12.5 - 40.0 mm |
>= 36300 psi @Strain 0.200 %, Thickness 0.492 - 1.57 in |
Temper T451; Standard EN 485-2 |
Constellium ALPLAN® 2017A High-Strength Rolled Precision Aluminum Plate, Milled Both Sides ALPLAN® 2017A precision plates combine a very good dimensional stability with a high level of mechanical strength and elongation. The outstanding flatness, the low roughness and high quality of the.. |
|||
Tensile Strength, Yield | 250 MPa @Thickness 3.20 mm, Temperature 760 °C |
36300 psi @Thickness 0.126 in, Temperature 1400 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, sheet, aged 100 hours at 899°C Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Tensile Strength, Yield | 250 MPa @Thickness 4.00 mm, Temperature 427 °C |
36300 psi @Thickness 0.157 in, Temperature 801 °F |
0.2% offset |
Haynes Hastelloy® C-4 alloy, sheet, heat treated at 1066°C, rapid quenched Nickel-chromium-molybdenum alloy with outstanding high-temperature stability as evidenced by high ductility and corrosion resistance even after aging in the 1200 to 1900°F (649 to 1038°C) range. T.. |
|||
Tensile Strength, Yield | 250 MPa @Strain 0.200 % |
36300 psi @Strain 0.200 % |
EN min.,RT; EN 10002-1 |
Outokumpu 725LN Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto) form. |