Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 110 MPa @Strain 0.200 %, Temperature 300 °C |
16000 psi @Strain 0.200 %, Temperature 572 °F |
EN min.; EN 10002-5 |
Outokumpu 4301 Cr-Ni Austenitic Stainless Steel General purpose steel with good corrosion resistance.Applications: Wide variety of applications in construction, chemical, petroleum, automobile, and domestic appliance markets.Available in hot roll.. |
|||
Tensile Strength, Yield | 110 MPa @Strain 0.200 %, Temperature 500 °C |
16000 psi @Strain 0.200 %, Temperature 932 °F |
EN min.; EN 10002-5 |
Outokumpu 4404 Cr-Ni-Mo Austenitic Stainless Steel General purpose steel with excellent corrosion resistance, particularly in the presence of halides.Applications: FiltersBraiding for hydraulic hosesShaftsFastenersMarine componentsAvailable in hot r.. |
|||
Tensile Strength, Yield | >= 110 MPa @Strain 0.200 % |
>= 16000 psi @Strain 0.200 % |
|
PSM Industries PolyAlloys MIM-2200 sintered Low Alloy Steel PolyAlloys Injected Metals, a division of PSM Industries, Inc., offers precision, High-Performance components for structural, magnetic and electronic applications that require a high degree of compl.. |
|||
Tensile Strength, Yield | 110 MPa @Thickness 1.57 mm |
16000 psi @Thickness 0.0620 in |
CW; ASTM D638 |
Industrial Laminates/Norplex NP842 Paper Base Laminate
(discontinued **) Description: Paper reinforced phenolic grade with controlled conductivity. Mechanical strength similar to NP611. NP842 is semi-conductive on the surfaces and through the laminate.Thickness Tested: 0.. |
|||
Tensile Strength, Yield | 110 MPa @Thickness 1.57 mm |
16000 psi @Thickness 0.0620 in |
LW; ASTM D638 |
Industrial Laminates/Norplex NP329 Cotton Fabric Description: Bleached linen with melamine resin system. Provides better arc resistance than NP320E. Also, resistant to ammonia based refrigerants. Hard, durable material should be heated to punch, .. |
|||
Tensile Strength, Yield | 110 MPa @Thickness 1.57 mm |
16000 psi @Thickness 0.0620 in |
CW; ASTM D638 |
Industrial Laminates/Norplex NP610 Paper Base Laminate Description: Phenolic paper based grade for mechanical applications. Good tensile, compressive and flexural strength. Primarily a machining material, but may be hot punched up to .093" thick.Thickne.. |
|||
Tensile Strength, Yield | 110 MPa @Thickness 1.10 - 1.60 mm, Temperature 982 °C |
16000 psi @Thickness 0.0433 - 0.0630 in, Temperature 1800 °F |
0.2% offset |
Haynes Hastelloy® S alloy, flat products Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
Tensile Strength, Yield | 110 MPa @Strain 0.200 %, Temperature 870 °C |
16000 psi @Strain 0.200 %, Temperature 1600 °F |
Hot-Rolled Plate, Solution-Annealed |
Special Metals INCOLOY® alloy 890 Ni-Cr-Fe Superalloy INCOLOY® alloy 890 (UNS N08890) is the latest addition to the INCOLOY alloy family of heat resistant alloys. Alloy 890 joins the existing INCOLOY products in offering high strength along with ex.. |
|||
Tensile Strength, Yield | >= 110 MPa @Strain 0.200 %, Thickness 150 - 500 mm |
>= 16000 psi @Strain 0.200 %, Thickness 5.91 - 19.7 in |
Temper 03 |
Constellium Alumold® 110 Aluminum Cast Sliced Plate Alumold®-110 has been specifically developed for low–pressure processing (thermoforming, RTM) of plastics and their composites. The material can also be used for prototype injection moulds. The ma.. |
|||
Tensile Strength, Yield | >= 110 MPa @Strain 0.200 %, Thickness 80.0 - 100 mm |
>= 16000 psi @Strain 0.200 %, Thickness 3.15 - 3.94 in |
Tempers O/H111; Standard EN 485-2 |
Constellium Planoxal® 50 Aluminum plate Planoxal®-50 plates differ from other standard EN-AW 5083 alloy products by their low level of residual stress. This specialty plate is also suitable for decorative anodizing. Planoxal®-50 is main.. |
|||
Tensile Strength, Yield | 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
ASTM D638 |
BASF Ultramid® 8202 L Intermediate PA6 (Conditioned) Description: Ultramid 8202 L-Intermediate is an unreinforced, low viscosity, non-lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. It is avai.. |