Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 124 PC UL rated HB as of 10/97. 200 series recommended when V-2 rating required. 17.5 MFR, for small, intricate parts. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® 221 PC 17.5 MFR, for small, intricate parts. Improved flame retardance.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 221R PC 17.5 MFR, for small, intricate parts. Improved flame retardance. Internal mold release. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 241 PC (Asia Pacific) 10.5 MFR. Improved flame retardance. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXD9945A PC (Asia Pacific) UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HP2 PC Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains m.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HP4R PC Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). ETO and steam sterilizable. Contains a h.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPS2R PC Med/high flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam and gamma sterilizable.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPS6 PC (Asia Pacific) Med/low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam e-beam and gamma sterilizable. .. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPS6 PC (Europe-Africa-Middle East) Med/low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam e-beam and gamma sterilizable. .. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® IR2240 PC UL rated HB. 200 series recommended when V-2 rating required. Nonhalogenated. MFR 10.5. Internal mold release. FDA food contact compliant in limited colors.This data was supplied by SABIC-IP for.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® IR2520 PC General purpose polycarbonate with melt flow rate of 8.5.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® OQ2320 PC Ophthalmic/safety lens market. OQ2xxx series in all transparent tints. Dedicated equipment, stringent quality production control.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® OQ2320 PC (Asia Pacific) Ophthalmic/safety lens market. OQ2xxx series in all transparent tints. Dedicated equipment, stringent quality production control.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® OQ2720 PC (Asia Pacific) Ophthalmic/safety lens market. OQ2xxx series in all transparent tints. Dedicated equipment, stringent production control conditions. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 141 PC (Asia Pacific) Nonhalogenated. 10.5 MFR. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 141R PC (Asia Pacific) Nonhalogenated. 10.5 MFR. Internal mold release. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® 141S PC (Asia Pacific) Nonhalogenated. 10.5 MFR. Internal mold release.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® 144 PC (Asia Pacific) LEXAN 144 is a medium viscosity multi purpose grade. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade is no longer supported with biocompatibility information .. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXRL0683 PC Copolymer 11 MFR LEXAN High Flow Ductile CopolymerThis data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXD9945A PC (Europe-Africa-Middle East) UV stabilzed Visualfx FR PC with non-brominated and non-chlorinated flame retardant systems. It is available Only in white diffused effect(WH8B111X) meeting UL-94 V0 at 2mm for thin wall application.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HP3REU PC (Europe-Africa-Middle East) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mold .. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HP6 PC Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mo.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS (Asia Pacific) 10% GR, ECO conforming FR, PC+ABS for thinwall molding applications. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP RZ006 PA 66 LNP THERMOCOMP* RZ006 is a compound based on Nylon 66 resin containing 30% Milled Glass. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Noryl LS175 PPE+HIPS (Europe-Africa-Middle East) Noryl* LS175 modified polyphenylene ether resin is an unfilled grade suitable for both extrusion and injection molding conversion routes. It uses non-chlorinated, non-brominated FR additives to del.. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6 LNP* STAT-LOY* PF303 is a Nylon 6 base resin containing 15% Glass Fiber. Added features of this grade includes: Antistat. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | ISO 527-2/50 |
Styron CALIBREâ„¢ MEGARAD 2081-HD-15 2 Polycarbonate Resin Overview: CALIBREâ„¢ MEGARAD 2081 HD-15 2 polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed .. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL EM7301F PPE+PS 10% glass-reinforced. HDT 252F. Good flow and polyurethane foam adhesion. Black only. |
|||
Tensile Strength at Break | 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HP4NR PC (Asia Pacific) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no m.. |