Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 5.93 MPa @Time 7200 sec |
860 psi @Time 2.00 hour |
Die C; ASTM D414 |
STAR Thermoplastic Alloys & Rubbers StarCLEAR CLR-1030 TPE Product Description: StarCLEAR CLR-1030 is an easy processing TPE designed for injection molding. Soft and ultra clear TPEs specifically targeted to medical, consumer and sporting goods market. Feat.. |
|||
Tensile Strength at Break | 5.93 MPa | 860 psi | ASTM D412 |
Teknor Apex Monprene® MP-2253 Thermoplastic Elastomer Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Fo.. |
|||
Tensile Strength at Break | 5.93 MPa | 860 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow FLEXOMER™ DFDA-1095 NT Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ DFDA-1095 NT is an ethylene-butene copolymer with a unique olefinic composition for improved process-ability and material handling. This product is produced via gas phase polymerization .. |
|||
Tensile Strength at Break | 5.93 MPa | 860 psi | 13.5 N/25mm |
Caplinq LINQTAPE™ PIT2A Product Description: LINQTAPE™ PIT-Series is a high-temperature resistant polyimide tape designed for both permanent and temporary bonding in many high temperature applications. Additionally, it p.. |
|||
Tensile Strength at Break | 5.93 MPa | 860 psi | 13.5 N/25mm |
Caplinq LINQTAPE™ PIT2S Product Description: LINQTAPE™ PIT-Series is a high-temperature resistant polyimide tape designed for both permanent and temporary bonding in many high temperature applications. Additionally, it p.. |
|||
Tensile Strength at Break | 5.93 MPa | 860 psi | Across Flow; ASTM D412 |
ExxonMobil Geolast® 701-70 Thermoplastic Elastomer A soft, black, oil resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good hot air and hot oil resistance for use in a wide range of applic.. |