Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 58.8 MPa @Thickness 3.20 mm |
8530 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
LG Chemical Lupox® GP2056F PBT+GF5% Description: Injection Molding, PBT+GF5%, Flame Retardant Application: IT/OA, E&E (Connector)CAS No. 71342-77-3, 65997-17-3, 24968-12-5 and 1309-64-4Information provided by LG Chemical |
|||
Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HA-1011 PC/ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® NH-1150HH PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® CF-1051 PC, Unreinforced High Impact High-impact material for the exterior material of mobile phoneInformation provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® HA-1011 PC/ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 58.8 MPa | 8530 psi | 50 mm/min; ASTM D638 |
Samsung Cheil Industries Infino® NH-1150HH PC/ABS, Unreinforced FR Information provided by Samsung Cheil Industries. |
|||
Tensile Strength at Break | 58.8 MPa | 8530 psi | ASTM D638 |
Unitika elitel UE3200 Polyester, Pellet Hard type standard Binder PaintUNITIKA l resins are thermoplastic saturated copolymeric polyester resins. l resins are expanding their applications from products such as adhesives, paints, ink bind.. |