- Polymer Property : Tensile Strength at Break = 7540 psi
Polymer Property : Tensile Strength at Break = 7540 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Cycoloy® CY9640 PC+ABS PC+ ABS, High Impact and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® BFL2000 PC (Asia Pacific) Non-Brominated, non-chlorinated flame retardant PC. Available in opaque white colors. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® CFR7630 PC COPOLYMER (Europe-Africa-Middle East) Lexan* CFR7630 Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm .. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER (Europe-Africa-Middle East) Lexan* LUX7636C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® ML7677A PC (Asia Pacific) Commercial grade for Polycarbonate in only nature color. Excellent processability, super high flow, flame retardant, UL rated V-1 at 2.0mm.This data was supplied by SABIC-IP for the Asia Pacific reg.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® BFL2000U PC (Europe-Africa-Middle East) Lexan* BFL2000U Polycarbonat (PC) resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating. Lexan* BFL2000U is designed for hig.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopolymer LNP* LUBRICOMP* KP003AXZ is a compound based on Acetal Homopolymer resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® EH7025AG PBT+PET (Asia Pacific) Valox EH7025AG is a mineral filled PBT/PET that offers good surface appearance, good flow and good heat performance. EH7025AG was developed for automotiove bezel application. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® EH7025AG PBT+PET (Europe-Africa-Middle East) Valox EH7025AG is a mineral filled PBT/PET that offers good surface appearance, good flow and good heat performance. EH7025AG was developed for automotiove bezel application. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® X4820 PBT+PC (Asia Pacific) Xenoy X4820 is a high modulus PC/PBT Blend. This resin provides high chemical resistance, excellent impact, very low creep, low CTE, excellent fatigue and dimensional stability. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® X4820 PBT+PC (Europe-Africa-Middle East) Xenoy X4820 is a high modulus PC/PBT Blend. This resin provides high chemical resistance, excellent impact, very low creep, low CTE, excellent fatigue and dimensional stability. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Europe-Africa-Middle East) PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ISO 527-1/-2 |
| Styrolution Polystyrol 165 H GR 2 PS Description: Polystyrol 165 H is a high molecular weight, good flowing grade, often blended with high impact extrusion grades.Applications: In blends with high impact Polystyrene or Styrolux; thermo.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Starex® TF-0930 MABS, Unreinforced Scratch Resistant Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Styrolution PS-168M Polystyrene Description: Polystyrene 168M is a high heat, high molecular weight general purpose polystyrene with excellent clarity and high stiffness. Due to its high melt strength and high stiffness. PS-168M i.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL NH5120 PPE+PS Noryl* NH5120 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated V1 flame re.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ASTM D638 |
| Supreme Petrochem SC 201E General Purpose Polystyrene CharacteristicsVery high molecular weight High heat grade Good melt strength Good clarity and mechanical strengthProcessing Extrusion MoldingApplicationsExtruded embossed sheets, OPS, foamed meat t.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL FXN121LG PPE+HIPS (Asia Pacific) Noryl* FXN121LG is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this r.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL FXN121LG PPE+HIPS (Europe-Africa-Middle East) Noryl* FXN121LG is an unfilled modified polyphenylene ether resin suitable for injection molding. Designed to possess a unique low gloss surface appearance even when molded in polished tools, this r.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| TPI Porene® GA800TW High Gloss/Weather Resistant/Antistatic Grade ABS INJECTION MOLDING; ANTISTATIC; WEATHER RESISTANT. HOUSING OF ELECTRICAL APPLIANCES, e.g. ELECTRIC FAN, TELEPHONE, CALCULATOR, TOYSPorene® is a registered trademark of Thai Petrochemical Industry C.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Eastman Eastar MN004 Copolyester Eastar Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar MN004 contains a mold release.Appl.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Eastman Tritan MX730 Copolyester Eastman Tritan Copolyester MX730 is an amorphous product with excellent appearance and clarity. Eastman Tritan Copolyester MX730 is a high flow medical grade of Eastman Tritan that has viscosity re.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
| Arkema Group Pebax® 5533 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® 5533 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is specially designed to food uses.Information provided by Arkema .. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50mm/min; ASTM D638 |
| 3M Dyneon™ PVDF 11008/0003 Polyvinylidene Fluoride PVDF is ideal for multiple applications across a wide array of industries. Widely used in the chemical processing, wire and cable, semiconductor, and oil and gas industries, PVDF is also gaining rec.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ISO 527-2 |
| Ascend Performance Materials Vydyne® 47H BK0644 Nylon 66, Impact Modified, DAM Vydyne® 47H BK0644 is a high-performance, medium-impact-modified, heat-stabilized PA66 resin with excellent UV stability and outstanding processing characteristics. This product has an UL746C f1 ra.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® LUX7636C PC COPOLYMER (Asia Pacific) Lexan* LUX7636C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U.. |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio. |
|||
| Tensile Strength at Break | 52.0 MPa @Temperature 23.0 °C |
7540 psi @Temperature 73.4 °F |
ISO 527 |
| DuPont Performance Polymers Hytrel® 7246HS NC010 TPC-ET
(Unverified Data**) Hytrel® 7246HS NC010 is a high modulus, heat stabilized grade with nominal hardness of 72D.Information provided by DuPont |
|||
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® LUX7630C PC COPOLYMER (Asia Pacific) Lexan* LUX7630C Polycarbonate (PC) resin is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm.. |
|||