Polymer Property : Tensile Strength at Break = 638 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 4.40 MPa	<= 638 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis LE0592 Polyethylene LE0592 is a crosslinkable black polyethylene compound, specially designed for bonded semi conductive screen applications. Applications: LE0592 is intended for semi conductive applications in XLPE m..
Tensile Strength at Break	<= 4.40 MPa	<= 638 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Supersmooth™ LE0550 Polyethylene Insulation Compound, Crosslinkable Supersmooth™ LE0550 is a crosslinkable black polyethylene compound, specially designed for bonded semiconductive screen applications. Applications: Supersmooth™ LE0550 is intended for semiconduct..
Tensile Strength at Break	<= 4.40 MPa	<= 638 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Supersmooth™ LE0592S Polyethylene Supersmooth™ LE0592S is a crosslinkable black polyethylene compound, specially designed for bonded semiconductive screen applications. Supersmooth™ LE0592S is intended for semiconductive applicat..
Tensile Strength at Break	<= 4.40 MPa	<= 638 psi	after aging (240h, 135°C); IEC 60811-1-2
Borealis Supersmooth™ LE8280 Polyethylene Insulation Compound, Crosslinkable Supersmooth™ LE8280 is a crosslinkable black polyethylene compound, specially designed for bonded semiconductive screen applications. Applications: Supersmooth™ LE8280 is intended for semiconduct..
Tensile Strength at Break	4.40 MPa	638 psi	ASTM D638
LG Chemical LC175 Polyolefin Elastomer for Polymer Modification Features: Improved impact strength in polypropylene; Excellent filler acceptance; Available as pellet form; Outstanding toughness with flexible performance; and Reduction of product weightApplicatio..