- Polymer Property : Tensile Strength at Break = 5950 psi
Polymer Property : Tensile Strength at Break = 5950 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer LNP LUBRICOMP* KX06415 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Powder. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics PREVEX VGAX PPE+PS Improved productivity and reliability. Nonchlorinated, nonbrominated flame retardant. 180F HDT. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 Type 1A |
| Solvay TECHNYL® eXten D 437P PA6.10 Description: TECHNYL® eXten D 437P is a high viscosity, unfilled, plasticized, UV and heat stabilized PA6.10 for extrusion applications. Technyl® eXten D 437P is a partially biosourced materia.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp RP0049 PA 66 LNP LUBRICOMP* RP0049 is a compound based on Nylon 66 resin containing Flame Retardant, PTFE, Silicone. Added features of this material include: Flame Retardant.This data was supplied by SABIC-IP f.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM STM1600 PEI Copolymer Siltem 1600 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity... |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 365 PET (Asia Pacific) Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031"". |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 460/461 Polyvinylidene Fluoride (PVDF) Solef® 460/461 PVDF homopolymer has high melt viscosity and is typically processed by extrusion.Features: High Viscosity; HomopolymerAdditional Properties: Crystallization Heat - ASTM D3418 46.0 .. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC (Asia Pacific) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® CL402 PBT+PC (Asia Pacific) XENOY CL402 is a high viscosity, unfilled, elastomer modified PC/PBT blend for extrusion/blowmolding applications. ISO1043-label: PC+PBT-I.This data was supplied by SABIC-IP for the Asia Pacific reg.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP HB006 PA 11 (Asia Pacific) LNP* Thermocomp* HB006 is a compound based on Nylon 11 resin containing Glass Bead. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ357M PBT+PC (Europe-Africa-Middle East) Valox* Resin IQ357M: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified, easy flow product with mold release. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® IQ357U PBT+PC (Europe-Africa-Middle East) Valox* Resin IQ357U: Environmentally responsible, low carbon footprint iQ* PBT + PC alloy. UL94 V-0 @0.63 mm. Impact modified and UV stabilized resin. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Valox® V3802 PBT + PC + PET (Asia Pacific) PBT + PC + PET, Mold Release, Flame retardant, Impact Modified, OpaqueThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-LOY W3000XXJ PBT LNP* STAT-LOY* W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Xenoy® X6320 PBT+PC (Asia Pacific) X6320 is a mineral filled PBT/PC resin developed for automotive painted doorhandles. Key advantages are excellent surface finish, easy processing and paint quality. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
| SABIC Innovative Plastics LNP THERMOCOMP MFB429 PP LNP* THERMOCOMP* MFB429 is a compound based on Polypropylene resin containing 10% Glass Fiber, 20% Glass Bead. Added features of this material include: Chemically Coupled, Flame Retardant. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
| Sumitomo Bakelite North America FM 21386 Synthetic Fiber Reinforced Phenolic Novolac FM 21386 is a single stage phenolic molding compound reinforced with synthetic fiber in pellet form.Information provided by Sumitomo Bak North America, Inc. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL PX1007 PPE+HIPS (Europe-Africa-Middle East) NORYL* PX1007 is an unfilled non-chlorinated, non-brominated flame retardant PPE/HIPS grade, targeted for flat panel TV enclosures. It has a Vicat B/120 temperature of 96 degC and UL-94 V0 @ 1.5mm .. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
| Denka MALECCA K-300 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ASTM D638 |
| Diapolyacrylate Shinko-Lac® U400B Transparent ABS Shinko-Lac® is a registered trademark of Diapolyacrylate Company Limited. Information provided by Dayson Polymers. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO R 527 |
| Fainplast Compounds R 211 Rigid PVC, Extrusion Shutters and shiny profiles |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO R 527 |
| Fainplast Compounds R 218 Rigid PVC, Extrusion Shutters and shiny profiles |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Hytrel® HTR8730 BK320 Polyester Elastomer TPC-ET
(Unverified Data**) 63 Shore D High Viscosity Polyester Elastomer with Excellent Mechanical Properties at Elevated Temperatures Developed for Blow MoldingInformation provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527-1/-2 |
| DuPont Performance Polymers Hytrel® SC969 NC010 Polyester Elastomer TPC-ET
(Unverified Data**) 63 Shore D High Performance Polyester Elastomer Developed for the Healthcare IndustryInformation provided by DuPont Performance Polymers |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type 1, 2"/min; ASTM D638 |
| Proto3000 PC-ABS Fused Deposition Modeling Polymer Description: PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials - the superior strength and heat resis.. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO R 527 |
| Fainplast Compounds R 244 Rigid PVC, Extrusion Shutters high modulus low curving |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL PX1005X PPE+PS PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. UL94 V0/5VA rated. UL746C F1. Excelent dielectric strength. Suitable for E/E market in indoor/outdoor applications. |
|||
| Tensile Strength at Break | 41.0 MPa | 5950 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HFD4471 PC Lexan* HFD4471 is a 10% glass filled, medium flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4417 has enhanced mold release, impact ductili.. |
|||