Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 379 - 448 MPa | 55000 - 65000 psi | Low Carbon Steel butt joint |
Lucas-Milhaupt BRAZE 380 Characteristics:Braze 380 is a free-flowing, low temperature filler metal with excellent wetting of most ferrous and non-ferrous base metals, and is a good substitute for cadmium-bearing filler meta.. |
|||
Tensile Strength at Break | 379 - 448 MPa | 55000 - 65000 psi | Low Carbon Steel butt joint |
Lucas-Milhaupt BRAZE 452 Characteristics:Braze 452 is a free-flowing, low temperature filler metal commonly used to replace cadmium-bearing filler metals of similar silver content. This alloy is best suited for narrow gap .. |
|||
Tensile Strength at Break | 379 - 414 MPa | 55000 - 60000 psi | Nickel-Silver butt joint |
Lucas-Milhaupt BRAZE 600 Silver Based Cadmium Free Filler Metal Characteristics: Braze 600 is a copper rich eutectiferous alloy, the eutectiferous portion of which is molten at 1300EF (705EC), about 25EF before the entire composition is completely fluid. Thus t.. |
|||
Tensile Strength at Break | 379 - 414 MPa | 55000 - 60000 psi | Nickel-Silver butt joint |
Lucas-Milhaupt BRAZE 650 (Easy) Silver Based Cadmium Free Filler Metal Characteristics: This alloy is a intermediate silver brazing filler metals with a slight tendency to liquate (i.e. separate into low and high melting constituents) if heated slowly through their mel.. |
|||
Tensile Strength at Break | 379 MPa | 55000 psi | Armco Iron (0.05% C) butt joint |
Lucas-Milhaupt EASY FLO 45 Silver Based Cadmium-Bearing Filler Metal Applications: Easy-Flo 45 is very versatile and can be used successfully on nearly all nickel, iron and copper base alloys. In certain instances, special fluxes, may be required to obtain good wet.. |
|||
Tensile Strength at Break | 379 MPa | 55000 psi | |
Mueller Ecostreamâ„¢ GreenDropâ„¢ C27451 DZR Lead Free Plumbing Brass To further compliment its EcoStreamâ„¢ family of alloys, Mueller Brass Company has developed a dezincification resistant version of its GreenDropâ„¢ C27450 Lead Free Brass Alloy. This new allo.. |
|||
Tensile Strength at Break | >= 379 MPa | >= 55000 psi | Any thickness |
Cadi 1815 Copper Alloy Zirconium addition to chromium copper improves creep resistance at high operating temperatures and reportedly reduces sticking of electrodes to the work during spot welding of galvanized materials. .. |
|||
Tensile Strength at Break | >= 379 MPa | >= 55000 psi | Any thickness |
Cadi 182 Copper Alloy Chromium copper is the primary copper alloy used for resistance spot and seam welding. This alloy achieves good hardness and electrical conductivity through a combination of heat treatment and cold .. |
|||
Tensile Strength at Break | 379 MPa | 55000 psi | Annealed |
California Fine Wire Copper, 27% Nickel Clad All values may vary dependent on specific design and usageCapabilities: WireRibbonSquareInsulatedPlatedInformation provided by California Fine Wire. |
|||
Tensile Strength at Break | >= 379 MPa | >= 55000 psi | |
Carlson C 200 Commercially Pure Nickel General DescriptionCarlson Alloy C 200 is commercially pure nickel, combining good mechanical properties with excellent resistance to many corrosive environments. This alloy retains its strength at.. |
|||
Tensile Strength at Break | >= 379 MPa | >= 55000 psi | |
Carlson C 201 Commercially Pure Nickel General DescriptionCarlson Alloy C 200 is commercially pure nickel, combining good mechanical properties with excellent resistance to many corrosive environments. This alloy retains its strength at.. |
|||
Tensile Strength at Break | 379 - 448 MPa | 55000 - 65000 psi | Low Carbon Steel butt joint |
Lucas-Milhaupt BRAZE 402 Silver Based Cadmium Free Filler Metal Characteristics: Braze 402 is a free-flowing, intermediate temperature filler metal and as such is a good substitute for cadmium-bearing filler metals with similar silver contents. The material is .. |