Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® FR15 ABS (Asia Pacific) Flame retardant ABS (non-PBBE additive). Good property/toughness. Excellent moldability. UL94 V-0/5VA rated. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycolac® FR23 ABS (Asia Pacific) Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® G320 ABS (Europe-Africa-Middle East) CYCOLAC G320 is a super high impact resistant ABS grade. It combines impact resistance with high stiffness, good temperature resistance and processability. It has a good fit in automotive interiors .. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® HMG47MD ABS General purpose, injection molding ABS for medical applications. Biocompatible (ISO10993). FDA compliant. Gamma & EtO sterilizable. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® MG47F ABS (Europe-Africa-Middle East) Multi-purpose, injection molding ABS providing a favorable balance of engineering properties. FDA compliant. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Cycolac® S701SU ABS (Europe-Africa-Middle East) CYCOLAC S701SU is an ABS with improved UV resistance, providing a superior balance of properties. Its wide processing window, excellent flow and good mechanical properties give this material an exce.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Asia Pacific) High heat PC/ABS blend offering high modulus / low CTE and good practical impact |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics GELOY CR8510 ASA ASA with outstanding UV exposure performance for both exterior and interior applications. F1 Rated. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO R 527 |
Fainplast Compounds RKS 320 Rigid PVC, Antishock Extrusion Lead Free Various profiles, antishock |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | DIN 53504 |
Huntsman IROGRAN® A 70 H 4673 M Polyester-Based TPU-Injection Molding Grade Introduction: IROGRAN A 70 H 4673 M is a soft polyester based thermoplastic polyurethane intended for injection molding applications. IROGRAN A 70 H 4673 M is part of the HUNTSMAN injection molding .. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | Injection molded parts; DIN 53504 |
Huntsman IROGRAN® A 85 E 5719 FCM TPU-Polyester Introduction: IROGRAN A 85 E 5719 FCM is a thermoplastic polyester polyurethane for melt calendering. IROGRAN is part of the HUNTSMAN technical extrusion and injection molding product range and offe.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | DIN 53504 |
Huntsman IROGRAN® A 85 P 4380 TPU-Polyether Introduction: IROGRAN A 85 P 4380 is a flame-retardant, halogen-free, thermoplastic polyether-polyurethane intended for extrusion and injection molding applications. Additional characteristics of th.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | MD |
JPJ Technologies LLD150-2 LLDPE Virgin Application: Used for ice & frozen bags, garbage bags consumer packingInformation provided by JPJ Technologies |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | |
LATI Latishield 36/SP-05A ABS, Steel Fiber Reinforced EMI shielding product based on Acrylonitrile-Butadiene-Styrene copolymer (ABS). Steel fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provid.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Xenoy® CL500U PBT+PC (Europe-Africa-Middle East) XENOY CL500U is a semi-crystalline blend, developed for exterior automotive parts ( except bumper shells ) and non automotive parts, requiring good impact, excellent chemical resistance and UV stabi.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp 5X06476 FP-V (PVDF) LNP* FP-VM-3830 is a compound based on Polyvinylidine Fluoride (PVDF) containing Mineral.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP MC002 PP LNP* THERMOCOMP* MC002 is a compound based on Polypropylene resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
Eastman Eastar CN015 Copolyester, High Flow Grade with Mold Release Applications:CompactsCosmetic jar capsCosmetic jarsCosmetics/personal care packagingFragrance capsFragrance packagingLip gloss containersLipstick containersPersonal care bottlesKey Attributes:Abilit.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D 638 |
Cossa Polimeri ESTALUX 9202 A Methyl Methacrylate Acrylonitrile Butadiene Styrene Plastic blend that combines impact properties of ABS with the excellent transparency of PMMAInformation provided by Cossa Polimeri S.r.l. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D 638 |
Cossa Polimeri ESTALUX 9202 Methyl Methacrylate Acrylonitrile Butadiene Styrene Plastic blend that combines impact properties of ABS with the excellent transparency of PMMABiomedical grade in line with US pharmacopeia class VI USP and European pharmacopeia cap. 3.2.2Information.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® L 20 H FR PA12 FR Product Description: Grilamid L 20 H FR is a flame retarded, medium viscosity product, based on Polyamide 12 (PA12). Grilamid L 20 H FR contains no halogen or phosphorus, it has a light natural colo.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ISO 527 |
Eurotec® Tecomid® NBX0 HF75 NL PA6, 75% heavy reinforced, improved flexibility, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM-D638 |
Braskem AD57 HDPE Monofilament Polyethylene Copolymer AD57 resin is a high-density polyethylene, copolymer of butene-1, produced by the solution process, designed for raffia extrusion, and Raschel knitted with excellent optical and mechanical propertie.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
Aclo Accucomp ABS ABS801L Medium Impact Grade |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (1.5 mm Molded Thickness) AZDEL SuperLite® SL550800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334M10L Mica Reinforced |
|||
Tensile Strength at Break | 35.0 MPa @Temperature 80.0 °C |
5080 psi @Temperature 176 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D3759 |
3M Scotch® 893 Filament Tape Scotch® Tape 893 is a general-purpose packaging tape reinforced with continuous glass-yarn filaments that give the tape high tensile strength and low stretch. The clear 3M™ Scotchpro™ backing pro.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | DIN EN ISO 527-3 |
3M Dyneon™ TF 2072Z PTFE Fine Powder Dyneon™ TF 2072 Z PTFE is an ideal grade for thin-wall, small diameter tubing and wire and cable insulations, processed by paste extrusion method at reduction ratio up to 3000:1. This product offer.. |
|||
Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527 |
Chi Mei Polylac® PA-746Y ABS
(discontinued **) Medium flow, high impact |