Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 30.4 MPa | 4410 psi | |
Taiwan PU Corporation TPU-BH85 Hydrolysis Resistance, Blow Molding Polyether Base TPU Thermoplastic Polyurethane (TPU), Hydrolysis Resistance, Polyether Base, Blow MoldingInformation provided by Taiwan PU Corporation. |
|||
Tensile Strength at Break | >= 30.4 MPa | >= 4410 psi | |
Sibur SKI-3 Superior Quality, 1st Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment. |
|||
Tensile Strength at Break | >= 30.4 MPa | >= 4410 psi | |
Sibur SKI-3 Superior Quality, 2nd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. For production of tires and rubber technical articles of wide assortment. |
|||
Tensile Strength at Break | >= 30.4 MPa | >= 4410 psi | |
Sibur SKI-3S Superior Quality, 1st Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. It is used instead of natural rubber during production of colored rubber articles, medical articles, and rubbers contacting with food products. |
|||
Tensile Strength at Break | >= 30.4 MPa | >= 4410 psi | |
Sibur SKI-3S Superior Quality, 2nd Group Isoprene Rubber (IR) Nipol-IR 2200, Natsyn-2200, Kraton-IR 401. It is used instead of natural rubber during production of colored rubber articles, medical articles, and rubbers contacting with food products. |
|||
Tensile Strength at Break | 30.4 MPa | 4410 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SP6433 9710 Medium Impact Polystyrene Characteristics High flow Good toughness Good shine Available in various colors Processing Injection molding Extrusion Applications Pipes & profiles for wiring Beading for furniture and tables .. |