Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 28.44 - 43.15 MPa | 4125 - 6258 psi | |
Taiwan PU Corporation PTMG CPU-100L Polyurethane Casting Elastomer A urethane elastomer that can be cured by reacting with a polyamine or a polyolhardener. The molding process is composed of pre-heating, degassing, maxing with a hardener, pouring into the mold, cu.. |
|||
Tensile Strength at Break | 28.44 - 42.17 MPa | 4125 - 6116 psi | |
Taiwan PU Corporation PTMG CPU-42L Polyurethane Casting Elastomer A urethane elastomer that can be cured by reacting with a polyamine or a polyolhardener. The molding process is composed of pre-heating, degassing, maxing with a hardener, pouring into the mold, cu.. |
|||
Tensile Strength at Break | 28.44 MPa | 4125 psi | |
Taiwan PU Corporation TPU-EH90 High Hydrolysis Resistance, Extrusion Molding Polyether Base TPU Thermoplastic Polyurethane (TPU), High Hydrolysis Resistance, Polyether Base, Extrusion MoldingInformation provided by Taiwan PU Corporation. |
|||
Tensile Strength at Break | 28.44 MPa @Temperature 100 °C, Time 1.21e+6 sec |
4125 psi @Temperature 212 °F, Time 336 hour |
After Dry Heat Aging; ASTM D865 |
Seals Eastern 7344 Highly Saturated Nitrile Rubber HNBR for Oil & Gas serviceInformation provided by Seals Eastern, Inc. |