Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 27.0 MPa | 3920 psi | |
Plastcom SLOVALEN PH 61 B 70 PP, 70% mineral filling FeaturesModified PP for injection moulding with the content of 70% of barium sulphate. Increased density. Decreased shrinkage.Used for production of vertical blind weights. Delivered in natural mode.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Polimeri Europa Sinkral® PD D 232/M4 ABS Resin Special very low gloss extrusion / co-extrusion grade, with good flow.Applications: Sinkral PD D 232/M4 is widely used in extrusion / co-extrusion of foils, when a very high matte appearance is req.. |
|||
Tensile Strength at Break | <= 27.0 MPa | <= 3920 psi | ISO/R527 |
Polykemi AB POLYfill PPHC T5040 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 27.0 MPa @Temperature 23.0 °C |
3920 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
DuPont Performance Polymers Hytrel® HTR8223 BK320 TPC-ET
(Unverified Data**) Hytrel® HTR8223 BK320 is designed for blow molding or processing techniques requiring high melt viscosity. It has nominal hardness of 42D, is pigmented black with fine particle size carbon black, a.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | after 7days @136°C; UL 1581 |
SABIC Innovative Plastics NORYL WCA871A PPE (Europe-Africa-Middle East) Flame retardant performance and mechanical properties capable of meeting UL VW-1 requirement and 105C temperature rating as defined UL1581. UL1581 tests conducted on 1.0mmD wire with AWG28 conductor.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCA875 PPE-TPE Non-halogenated flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced t.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCA875 PPE-TPE (Asia Pacific) Non-halogenated flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced t.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCA875 PPE-TPE (Europe-Africa-Middle East) Non-halogenated flame retardant Flexible Noryl extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Excellent flame retardant performance with balanced t.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | after 7days @136°C; UL 1581 |
SABIC Innovative Plastics NORYL WCA901 PPE-TPE (Asia Pacific) Non-Halogenated flame retardant, flexible Noryl resin intended for evaluation in wire and cable applications, capable of meeting VW-1 and 105°C end use temperature requirements as defined by UL.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp ML002S PP LNP* Lubricomp* ML002S is a compound based on Polypropylene containing PTFE. Characteristics of this grade are: Heat Stabilized and Internally Lubricated.This data was supplied by SABIC-IP for the.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP ML003S PP LNP* LUBRICOMP* ML003S is a compound based on Polypropylene resin containing 15% PTFE. Added features include: Heat Stabilized, Wear Resistant. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON AX01706 ABS LNP* STAT-KON* AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. |
|||
Tensile Strength at Break | >= 27.0 MPa | >= 3920 psi | |
Shandong Dongyue Shenzhou New Material Co DS602 Perfluorinated Ethylene-Propylene Copolymer Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene resin is the copolymer of the TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-loy A3000Z ABS (Asia Pacific) LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for t.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Sumitomo Bakelite North America SI 9002N-1 Silicone Compound Short fibergass reinforced silicone molding compound which offers moderate strength properties, dimensional stability, and excellent long-term thermal stability at elevated temperatures.Information .. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | 50 mm/min; ASTM D638 |
Supreme Petrochem SP 6411 1924 Light Stabilized Polystyrene Characteristics Prevents dust patterns due to static charges High gloss Good flow Improved light fastness Processing Injection molding Extrusion Applications A/C and cooler grill Material Status.. |
|||
Tensile Strength at Break | >= 27.0 MPa | >= 3920 psi | ASTM D638 |
UBE P7115U Electronic Grade Nylon Copolymer Powder Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
Tensile Strength at Break | >= 27.0 MPa | >= 3920 psi | ASTM D638 |
UBE 7115U Nylon 6/12 Copolymer Description: UBESTA Nylon 12 CopolymerInformation provided by UBE. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | 50 mm/min; ISO 527 |
Chi Mei Polyrex® PH-60 Polystyrene - High Impact Medium impact |
|||
Tensile Strength at Break | 27.0 - 35.0 MPa | 3920 - 5080 psi | ASTM D638 |
Daikin NEOFLON AP-201 PFA Pellets NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Complicated injection molded parts requiring high melt flow to fil.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0334M30CL Mica Reinforced Coupled |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0336M10CL Mica Reinforced Coupled |
|||
Tensile Strength at Break | 27.0 MPa @Temperature 120 °C |
3920 psi @Temperature 248 °F |
ISO Data |
BASF Ultramid® 8260 HS BK-102 40% Mineral Filled PA6 (Conditioned) Ultramid 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined wi.. |
|||
Tensile Strength at Break | 27.0 - 48.0 MPa | 3920 - 6960 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2850 Black Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating, pigmented. High stability in harsh thermal, chemical and ultraviolet environments. High toughness .. |
|||
Tensile Strength at Break | 27.0 - 48.0 MPa | 3920 - 6960 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2850-04 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339M10L Mica Reinforced |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
Arkema Group EVATANE® 24-03 Copolymer Ethylene - Vinyl Acetate EVATANE® 24-03 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 24-03 is stabilized with antioxidants. The High Vinyl Acetate co.. |
|||
Tensile Strength at Break | <= 27.0 MPa | <= 3920 psi | ISO/R527 |
Polykemi AB POLYfill PPHC K5020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Tensile Strength at Break | 27.0 MPa | 3920 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP CL002 PS (Europe-Africa-Middle East) LNP* LUBRICOMP* CL002 is a compound based on Polystyrene resin containing PTFE. Added features include: Internally Lubricated. |