Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 234 MPa | 33900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP RF00C PA 66 (Europe-Africa-Middle East) LNP* Thermocomp* RF00C is a compound based on Nylon 66 resin containing Glass Fiber. |
|||
Tensile Strength at Break | 234 MPa | 33900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP UF008AR PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UF008AR is a compound based on Polyphthalamide resin, containing Glass Fiber. Added features include; Mold Release. |
|||
Tensile Strength at Break | 234 MPa | 33900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP UF008AS PPA (Europe-Africa-Middle East) LNP* THERMOCOMP* UF008AS is a compound based on Polyphthalamide resin, containing Glass Fiber. Added features include; Mold Release. |
|||
Tensile Strength at Break | 234 MPa | 33900 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP UX06028 PPA (Europe-Africa-Middle East) LNP * THERMOCOMP* UX06028 is a compund based on Polyphthalamide resin, containing Glass Fiber. Added features include Mold Release. |
|||
Tensile Strength at Break | 234 MPa | 33900 psi | ASTM D638 |
SABIC Innovative Plastics LNP VERTON RVL28 PA 66 LNP* VERTON* RVL28 is a compound based on Nylon 66 resin containing 40% Long Glass Fiber, 10% PTFE. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant, Structura.. |
|||
Tensile Strength at Break | 234 MPa | 33900 psi | 0.2 in/min; ASTM Test |
BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Dry) Ultramid 1603-2 NF2004 is a 43% glass reinforced, heat stabilized injection molding nylon 6/6 with the highest level of glass reinforcement for maximum strength and stiffness. |