Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 2.21 MPa | 321 psi | JRF- 72 hrs @ 60°C, and 72 hrs @ 49°C Air Drying, and 7 days @ 121°C |
3M AC-350 Class A-1 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.21 MPa | 321 psi | JRF- 72 hrs @ 60°C, and 72 hrs @ 49°C Air Drying, and 7 days @ 121°C |
3M AC-350 Class A-1/2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Tensile Strength at Break | 2.21 MPa | 321 psi | JRF- 72 hrs @ 60°C, and 72 hrs @ 49°C Air Drying, and 7 days @ 121°C |
3M AC-350 Class A-2 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |